Polymer Property : Tensile Strength, Ultimate = 1120 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	1120 MPa @Temperature 540 Â°C	162000 psi @Temperature 1000 Â°F
Haynes X-750 Nickel Alloy Sheet and Strip (AMS 5598, UNS N07750) Haynes X-750 (UNS No. N07750) alloy is an age-hardenable, nickel-base superalloy with very good strength at temperatures up to about 1600Â°F (870Â°C). It is widely used as a wrought material for..
Tensile Strength, Ultimate	1120 MPa @Thickness 12.7 mm, Temperature 25.0 Â°C	162000 psi @Thickness 0.500 in, Temperature 77.0 Â°F	As Welded and Aged at 1850Â°F(1010Â°C)/2hr/AC + 1450Â°F(788Â°C)/8h/AC; Weld/Weld Fracture
Haynes 282Â® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate Excellent High Temperature Strength HAYNESÂ® 282Â® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la..
Tensile Strength, Ultimate	1120 MPa @Temperature 550 Â°C	162000 psi @Temperature 1020 Â°F	Precipitation Hardened prior to test
Special Metals INCONELÂ® Alloy X-750 A nickel-chromium alloy similar to INCONEL alloy 600 but made precipitation hardenable by additions of aluminum and titanium. The alloy has good resistance to corrosion and oxidation along with hig..
Tensile Strength, Ultimate	1120 MPa @Thickness 25.4 mm, Temperature 25.0 °C	162000 psi @Thickness 1.00 in, Temperature 77.0 °F	Welded then age-hardened
Haynes Hastelloy® C-22HS™ Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately doubl..