Polymer Property : Tensile Strength, Ultimate = 109000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English
Tensile Strength, Ultimate	750 MPa @Thickness 12.7 mm, Temperature 149 Â°C	109000 psi @Thickness 0.500 in, Temperature 300 Â°F
Haynes HastelloyÂ® Hybrid-BC1Â® Nickel Alloy Shielded Metal Arc Welded (SMAW) Plate HASTELLOYÂ® HYBRID-BC1Â® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing..
Tensile Strength, Ultimate	751 MPa @Thickness 9.50 - 25.4 mm, Temperature 427 Â°C	109000 psi @Thickness 0.374 - 1.00 in, Temperature 801 Â°F
Haynes HastelloyÂ® S alloy, flat products Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Tensile Strength, Ultimate	752 MPa @Thickness 25.4 mm	109000 psi @Thickness 1.00 in
Haynes HastelloyÂ® C-2000Â® alloy, flat products Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h..
Tensile Strength, Ultimate	752 MPa @Thickness 1.60 mm	109000 psi @Thickness 0.0630 in
Haynes HastelloyÂ® C-2000Â® alloy, flat products Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h..
Tensile Strength, Ultimate	752 MPa @Thickness 46.1 mm, Temperature 20.0 Â°C	109000 psi @Thickness 1.81 in, Temperature 68.0 Â°F
Haynes HastelloyÂ® C-22Â® alloy, transverse, GMAW short arc weldment, plate HASTELLOYÂ® C-22Â® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an..
Tensile Strength, Ultimate	754 MPa @Temperature 200 Â°C	109000 psi @Temperature 392 Â°F
Haynes HastelloyÂ® C-22HSâ„¢ Nickel Alloy Sheet, Cold-rolled, Solution Annealed Outstanding Corrosion Resistance, High Strength HASTELLOYÂ® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou..
Tensile Strength, Ultimate	754 MPa @Thickness 3.20 mm, Temperature 260 Â°C	109000 psi @Thickness 0.126 in, Temperature 500 Â°F
Haynes HastelloyÂ® Hybrid-BC1Â® Nickel Alloy Sheet, Cold Rolled and Solution Annealed HASTELLOYÂ® HYBRID-BC1Â® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing..
Tensile Strength, Ultimate	750 MPa @Temperature 260 °C	109000 psi @Temperature 500 °F
Crucible Steel XM-19 Stainless Steel Crucible XM-19 Stainless is a nitrogen strengthened, low carbon, austenitic, stainless steel that provides good corrosion resistance in combination with high strength. The alloy has better corrosio..
Tensile Strength, Ultimate	752 MPa @Thickness 12.7 mm, Temperature 20.0 °C	109000 psi @Thickness 0.500 in, Temperature 68.0 °F
Haynes Hastelloy® C-22® alloy, transverse, GTAW short arc weldment, plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al..
Tensile Strength, Ultimate	749 MPa @Thickness 19.1 mm, Temperature 149 °C	109000 psi @Thickness 0.752 in, Temperature 300 °F
Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Plate, Hot Rolled and Solution Annealed HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing spe..
Tensile Strength, Ultimate	750 MPa @Temperature 800 °C	109000 psi @Temperature 1470 °F
Haynes 282® Nickel Alloy Plate, Solution Annealed and Age-Hardened Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and land-b..