Polymer Property : Tensile Strength, Ultimate = 101000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 699 MPa

@Thickness 12.7 mm,
Temperature 316 °C
 101000 psi

@Thickness 0.500 in,
Temperature 601 °F
Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Shielded Metal Arc Welded (SMAW) Plate
HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing..
Tensile Strength, Ultimate 695 MPa

@Temperature 300 °C
 101000 psi

@Temperature 572 °F
Haynes Hastelloy® C-22HS™ Nickel Alloy Plate and Bar, Hot-rolled, Solution Annealed
Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou..
Tensile Strength, Ultimate 695 MPa

@Thickness 1.60 - 4.70 mm,
Temperature 204 °C
 101000 psi

@Thickness 0.0630 - 0.185 in,
Temperature 399 °F
Haynes Hastelloy® C-276 alloy, solution heat treated flat products
Hastelloy® C-276 alloy is a nickel-molybdenum-chromium wrought alloy that is a versatile corrosion-resistant alloy. C-276 alloy is an improved wrought version of alloy C in that it usually doesn'..
Tensile Strength, Ultimate 696.4 MPa

@Thickness 2.40 mm,
Temperature 204 °C
 101000 psi

@Thickness 0.0945 in,
Temperature 399 °F
Haynes Hastelloy® C-276 alloy, solution heat treated flat products
Hastelloy® C-276 alloy is a nickel-molybdenum-chromium wrought alloy that is a versatile corrosion-resistant alloy. C-276 alloy is an improved wrought version of alloy C in that it usually doesn'..
Tensile Strength, Ultimate 696 MPa

@Thickness 12.7 mm,
Temperature 25.0 °C
 101000 psi

@Thickness 0.500 in,
Temperature 77.0 °F
Haynes Hastelloy® G-35® Nickel Alloy Gas Tungsten Arc Welded (GTAW) Plate
Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process” phosphoric acid, which is widely used in the production of fertilizers. Tests indicat..
Tensile Strength, Ultimate 696 MPa

@Thickness 12.7 mm,
Temperature 316 °C
 101000 psi

@Thickness 0.500 in,
Temperature 601 °F
Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Gas Tungsten Arc Welded (GTAW) Plate
HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing..
Tensile Strength, Ultimate 696 MPa

@Temperature 23.0 °C
 101000 psi

@Temperature 73.4 °F
ATI Allegheny Ludlum Stainless Steel Type 201, Annealed (UNS S20100)
Allegheny Ludlum Type 201 and 201L have the greatest tonnage of the Cr-Ni-Mn steels (200 series). Type 201 provides advantages over the 18-8 grades in certain applications. Lower cost manganese an..
Tensile Strength, Ultimate 694 MPa

@Thickness 9.50 mm,
Temperature 204 °C
 101000 psi

@Thickness 0.374 in,
Temperature 399 °F
Haynes Hastelloy® C-4 alloy, sheet, aged 100 hours at 899°C
Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T..
Tensile Strength, Ultimate 696 MPa

@Diameter 12.7 mm,
Temperature 25.0 °C
 101000 psi

@Diameter 0.500 in,
Temperature 77.0 °F
Haynes Hastelloy® G-35® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform
Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process” phosphoric acid, which is widely used in the production of fertilizers. Tests indicate that it is..