Polymer Property : Tensile Strength, Ultimate = 100000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	691 MPa @Temperature 500 Â°C	100000 psi @Temperature 932 Â°F
Haynes HastelloyÂ® C-22HSâ„¢ Nickel Alloy Sheet, Cold-rolled, Solution Annealed Outstanding Corrosion Resistance, High Strength HASTELLOYÂ® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou..
Tensile Strength, Ultimate	692 MPa @Temperature 93.0 Â°C	100000 psi @Temperature 199 Â°F
Haynes HastelloyÂ® G-35Â® Nickel Alloy Plate, Annealed at 2075Â°F (1135Â°C) Known for its corrosion performance, HASTELLOYÂ® G-35Â® alloy was designed to resist â€œwet processâ€ phosphoric acid, which is widely used in the production of fertilizers. Tests indicat..
Tensile Strength, Ultimate	692 MPa @Thickness 12.7 mm, Temperature 427 Â°C	100000 psi @Thickness 0.500 in, Temperature 801 Â°F
Haynes HastelloyÂ® Hybrid-BC1Â® Nickel Alloy Gas Tungsten Arc Welded (GTAW) Plate HASTELLOYÂ® HYBRID-BC1Â® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing..
Tensile Strength, Ultimate	690 MPa @Temperature 23.0 Â°C	100000 psi @Temperature 73.4 Â°F
Special Metals INCONELÂ® Alloy G-3 A nickel-chromium-iron alloy with additions of molybdenum and copper. It has good weldability and resistance to intergranular corrosion in the welded condition. The low carbon content helps preven..
Tensile Strength, Ultimate	690 - 980 MPa @Diameter 63.0 mm	100000 - 142000 psi @Diameter 2.48 in	Rm. Core strength in hardened condition.
Assab Steels 7210M Machinery Steel ASSAB 7210M is an alloyed case hardening steel with high core strength.Applications: ASSAB 7210M is used for applications requiring a hard, wear resistant surface and a tough core, such as transmiss..
Tensile Strength, Ultimate	692 MPa @Thickness 19.1 mm, Temperature 316 °C	100000 psi @Thickness 0.752 in, Temperature 601 °F
Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Plate, Hot Rolled and Solution Annealed HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing spe..
Tensile Strength, Ultimate	692 MPa @Temperature 93.0 °C	100000 psi @Temperature 199 °F
Haynes Hastelloy® G-35® Nickel Alloy Bar, Annealed at 2075°F (1135°C) Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process” phosphoric acid, which is widely used in the production of fertilizers. Tests indicate that it is..