Polymer Property : Film Tensile Strength at Yield, TD = 75.8 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, TD	59.3 - 75.8 MPa	8600 - 11000 psi	ASTM D882
Honeywell CapranÂ® Oxyshieldâ„¢ M-OPA (0.60 mil) Monoaxially Oriented, Co-Extruded In-Line Nylon6/Nylon6/Nylon6 Film Description: CapranÂ® Oxyshieldâ„¢ M-OPA (Machine Direction Oriented Polyamide) is a clear, monoaxially oriented, co-extruded in-line nylon6/nylon6/nylon6 film with high mechanical strength and..
Film Tensile Strength at Yield, TD	59.3 - 75.8 MPa	8600 - 11000 psi	ASTM D882
Honeywell CapranÂ® Oxyshieldâ„¢ M-OPA (0.75 mil) Monoaxially Oriented, Co-Extruded In-Line Nylon6/Nylon6/Nylon6 Film Description: CapranÂ® Oxyshieldâ„¢ M-OPA (Machine Direction Oriented Polyamide) is a clear, monoaxially oriented, co-extruded in-line nylon6/nylon6/nylon6 film with high mechanical strength and..
Film Tensile Strength at Yield, TD	59.3 - 75.8 MPa	8600 - 11000 psi	ASTM D882
Honeywell CapranÂ® Oxyshieldâ„¢ M-OPA (1.0 mil) Monoaxially Oriented, Co-Extruded In-Line Nylon6/Nylon6/Nylon6 Film Description: CapranÂ® Oxyshieldâ„¢ M-OPA (Machine Direction Oriented Polyamide) is a clear, monoaxially oriented, co-extruded in-line nylon6/nylon6/nylon6 film with high mechanical strength and..
Film Tensile Strength at Yield, TD	66.2 - 75.8 MPa	9600 - 11000 psi	ASTM D882
Honeywell CapranÂ® Oxyshieldâ„¢ OMBS (0.60 mil) Monoaxially Oriented, Co-Extruded Nylon6/EVOH/Nylon 6 Clear Film Description: Oxyshieldâ„¢ Oriented Medium Barrier is a 0.60 mil (15 micron) monoaxially oriented, coextruded nylon 6/EVOH/nylon 6 clear film with slip additive having excellent gas barrier throug..
Film Tensile Strength at Yield, TD	66.2 - 75.8 MPa	9600 - 11000 psi	ASTM D882
Honeywell CapranÂ® Oxyshieldâ„¢ OMBS (1.00 mil) Monoaxially Oriented, Co-Extruded Nylon 6-Based Clear Film Description: Oxyshieldâ„¢ Oriented Medium Barrier is a 1.00 mil (25 micron) monoaxially oriented, coextruded nylon 6/EVOH/nylon 6 clear film with slip additive having excellent gas barrier throug..