Polymer Property : Shear Modulus = 67.0 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English
Shear Modulus	67.0 GPa @Temperature 677 Â°C	9720 ksi @Temperature 1250 Â°F
Haynes R-41 alloy, 0.635 mm thick sheet, solution heat treated at 1079Â°C, water quenched, 30 minutes at 1066Â°C, aged 16 hours at 760Â°C (1400Â°F), air cooled Vacuum melted, exceptionally high strength at temperature between 649-982Â°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Shear Modulus	67.0 GPa @Temperature 677 Â°C	9720 ksi @Temperature 1250 Â°F
Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079Â°C, water quenched, 30 minutes at 1066Â°C, aged 16 hours at 760Â°C (1400Â°F), air cooled Vacuum melted, exceptionally high strength at temperature between 649-982Â°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Shear Modulus	67.0 GPa @Temperature 677 Â°C	9720 ksi @Temperature 1250 Â°F
Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079Â°C, water quenched, 30 minutes at 1066Â°C, air cooled, aged 16 hours at 760Â°C (1400Â°F) Vacuum melted, exceptionally high strength at temperature between 649-982Â°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Shear Modulus	67.0 GPa	9720 ksi
Ceramic Process Systems AlSiC-10, 54 vol% SiC Aluminum alloy A356.2 used. Hermeticity < 1x109 atm-cc/s He.CPS fabricates AlSiC by preparing an SiC preform which is subsequently infiltrated by molten aluminum metal. After infiltration, compone..