Polymer Property : Shear Modulus = 0.0250 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Shear Modulus	0.0250 - 1.00 GPa @Temperature 50.0 - 225 °C	3.63 - 145 ksi @Temperature 122 - 437 °F	Average value: 0.688 GPa Grade Count:5
Overview of materials for Polysulfone (PSU) This property data is a summary of similar materials in the MatWeb database for the category "Polysulfone". Each property range of values reported is minimum and maximum values of appropriate MatWeb..
Shear Modulus	>= 0.0250 GPa	>= 3.63 ksi	ASTM C393
3A Composites Core Materials AIREX® T90.150 Easy Processing Structural FST Foam AIREX® T90 is a closed-cell, thermoplastic and recyclable polymer foam with excellent fire, smoke & toxicity (FST) properties. It has very good mechanical properties and a good resistance to fatigu..
Shear Modulus	>= 0.0250 GPa	>= 3.63 ksi	ASTM C393
3A Composites Core Materials AIREX® T92.130 Easy Processing Structural Foam AIREX® T92 is a closed-cell, thermoplastic and recyclable polymer foam with very good mechanical properties and price / performance ratio. It has a good resistance to fatigue, is chemically stable,..
Shear Modulus	>= 0.0250 GPa	>= 3.63 ksi	ASTM C393
3A Composites Core Materials AIREX® R82.110 High Performance Structural Foam AIREX® R82 is a closed-cell, thermoplastic polymer foam that combines outstanding fire resistance with low smoke and toxicity, along with excellent dielectric properties. It has a good strength to ..
Shear Modulus	>= 0.0250 GPa	>= 3.63 ksi	ASTM C393
3A Composites Core Materials AIREX® C71.75 Elevated Temperature Structural Foam AIREX® C71 is a closed cell, crosslinked polymer foam especially formulated to maintain its stability also at higher processing or service temperatures. It combines excellent stiffness and strength..
Shear Modulus	0.0250 - 0.950 GPa @Temperature 50.0 - 200 °C	3.63 - 138 ksi @Temperature 122 - 392 °F	Average value: 0.669 GPa Grade Count:1
Overview of materials for Polysulfone, 20% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polysulfone, 20% Glass Fiber Reinforced". Specific grades with glass content between 15% and 24% are inc..
Shear Modulus	0.0250 - 0.950 GPa @Temperature 50.0 - 200 °C	3.63 - 138 ksi @Temperature 122 - 392 °F	Average value: 0.669 GPa Grade Count:1
Overview of materials for Polysulfone, 30% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polysulfone, 30% Glass Fiber Reinforced". Specific grades with glass content between 25% and 34% are inc..