Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Modulus | 9.37 GPa | 1360 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP RFL449 PA 66 LNP* LUBRICOMP* RFL449 is a compound based on Nylon 66 resin containing 20% Glass Fiber, 20% PTFE. Added features of this grade include: Wear Resistant, Flame Retardant. |
|||
Tensile Modulus | 9.37 GPa | 1360 ksi | 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP IX95700 PA 6/12 (Asia Pacific) LNP* Thermocomp* IX95700 is a compound based on Nylon 6/12 resin containing Glass Fiber. |
|||
Tensile Modulus | 9.37 GPa | 1360 ksi | 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP IX95700 PA6.12 LNP* THERMOCOMP* IX95700 is a compound based on Nylon 6/12 resin containing Glass Fiber. |