Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Modulus | 4.89 GPa | 709 ksi | 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP ZX05506 PPE+PS LNP LUBRICOMP* ZX05506 is a compound based on PPE+PS Blend resin containing Graphite Powder, PTFE. Added features of this material include: Internally Lubricated. |
|||
Tensile Modulus | 4.89 GPa | 709 ksi | 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP ZX05506 PPE+PS (Asia Pacific) LNP LUBRICOMP* ZX05506 is a compound based on PPE+PS Blend resin containing Graphite Powder, PTFE. Added features of this material include: Internally Lubricated. |
|||
Tensile Modulus | 4.89 GPa | 709 ksi | 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRILOY RF203H PA 66 LNP LUBRILOY* RF203H is a compound based on Nylon 66 resin containing 15% Glass Fiber, Proprietary Lubricant. Added features of this material include: Wear Resistant, Healthcare. |
|||
Tensile Modulus | 4.89 GPa | 709 ksi | 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRILOY RF203XXH PA 66 LNP* LUBRILOY* RF203XXH is a compound based on Nylon 66 resin containing 15% Glass Fiber, Proprietary Lubricant. Added features of this material include: Wear Resistant, Healthcare. |