Polymer Property : Tensile Modulus = 4.82 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Modulus	4.82 GPa	699 ksi	5 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® JK500 PC+ABS (Asia Pacific) 10% GR, ECO conforming FR, PC+ABS for thinwall molding applications.
Tensile Modulus	4.82 GPa	699 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP STAT-LOY 9X03508 PPO+PA66 LNP* STAT-LOY* 9X03508 is a compound based on PPO+PA66 resin containing Proprietary Filler(s). Added features of this material include: Antistatic, Flame Retardant, High Impact.
Tensile Modulus	4.82 GPa	699 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP STAT-LOY 9X03508 PPO+PA66 (Asia Pacific) LNP* Stat-loy* 9X03508 is a compound based on PPO+PA66 resin containing Flame Retardant, Anti-Static. Added features of this material include: Antistat, Flame Retardant, High Impact.
Tensile Modulus	4.82 GPa	699 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP DF003E PC LNP* Thermocomp* DF003E is a compound based on Polycarbonate resin containing 15% Glass Fiber. Added features of this material include: Easy Molding.
Tensile Modulus	4.82 GPa	699 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP DF003E PC (Asia Pacific) LNP* Thermocomp* DF003E is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Easy Molding.
Tensile Modulus	4.82 GPa	699 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP Thermocomp EB004 PEI LNP* Thermocomp* EB004 is a compound based on Polyetherimide resin containing Glass Bead.This data was supplied by SABIC-IP for the Americas region.
Tensile Modulus	4.82 GPa	699 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP Thermocomp EB004 PEI (Asia Pacific) LNP* Thermocomp* EB004 is a compound based on Polyetherimide resin containing Glass Bead.This data was supplied by SABIC-IP for the Asia Pacific region.
Tensile Modulus	4.82 GPa	699 ksi	5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP Lexan_JK500 PC+ABS LNP* Thermocomp* Lexan_JK500 compound is a 10% GR, ECO conforming FR, PC+ABS for thinwall molding applications.
Tensile Modulus	4.82 GPa	699 ksi	5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP Lexan_JK500 PC+ABS (Asia Pacific) 10% GR, ECO conforming FR, PC+ABS for thinwall molding applications.
Tensile Modulus	4.82 GPa	699 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOTUF RF002I PA 66 LNP THERMOTUF* RF002I is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: High Impact.
Tensile Modulus	4.82 GPa	699 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOTUF RF002I PA 66 (Asia Pacific) LNP* THERMOTUF* RF002I is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: High Impact.
Tensile Modulus	4.82 GPa	699 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOTUF MF004AI PP LNP* Thermotuf* MF004AI is a compound based on Polypropylene resin containing Glass Fiber. Added features of this material include: High Impact.
Tensile Modulus	4.82 GPa	699 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOTUF MF004AI PP (Asia Pacific) LNP* Thermotuf* MF004AI is a compound based on Polypropylene resin containing Glass Fiber. Added features of this material include: High Impact.
Tensile Modulus	4.82 GPa @Temperature 80.0 °C	699 ksi @Temperature 176 °F	ISO Data
BASF Ultramid® 8233G HS BK-102 33% Glass Filled PA6 (Dry) Ultramid 8233G HS BK-102 is a heat stabilized, weather resistant, 33% glass fiber reinforced PA6 injection molding compound offering excellent strength, stiffness, high temperature performance and d..