Polymer Property : Tensile Strength, Yield = 71800 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English
Tensile Strength, Yield	495 MPa @Strain 0.200 %, Temperature 540 Â°C	71800 psi @Strain 0.200 %, Temperature 1000 Â°F
Haynes 214Â® alloy, hot rolled solution annealed plate 12.7 mm (1/2 in.) thick Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Tensile Strength, Yield	495 MPa @Strain 0.200 %	71800 psi @Strain 0.200 %
Haynes 214Â® alloy, sheet, 1000 hours exposure at 870Â°C (1600Â°F) Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Tensile Strength, Yield	495 MPa @Strain 0.200 %	71800 psi @Strain 0.200 %
Haynes 230Â® alloy, 30% cold reduction, 1121Â°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149Â°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic..
Tensile Strength, Yield	495 MPa @Strain 0.200 %	71800 psi @Strain 0.200 %
Haynes 25 alloy, room temperature after 20% cold reduction, 1175Â°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980Â°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Tensile Strength, Yield	495 MPa @Strain 0.200 %	71800 psi @Strain 0.200 %
Haynes 25 alloy, room temperature sheet after 100 hours of 870Â°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980Â°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Tensile Strength, Yield	495 MPa @Strain 0.200 %	71800 psi @Strain 0.200 %
Haynes 230® alloy, 50% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat..