Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 480 - 560 MPa | 69600 - 81200 psi | Solution Annealed and Aged |
Materion Beryllium Copper Alloy 10C Castings (UNS C82000) Pouring Temperature: 1095-1175°CHeat treatment required for max strength (Annealing): 870-900°C/water quenchHeat treatment required for max strength (Hardening): 870-900°C/water quenchTabul.. |
|||
Tensile Strength, Yield | 480 - 660 MPa | 69600 - 95700 psi | |
Materion Beryllium Copper Alloy 190 Strip; AM (TM00) Temper (UNS C17200) Treatment required for max strength: Mill HardenedStress Relaxation-% Stress Remaining after 1000 hrs @ 100°C: 97%Stress Relaxation after 1000 hrs @ 200°C: 67%Formability Ratio, 90° Bend, R.. |
|||
Tensile Strength, Yield | 480 - 655 MPa | 69600 - 95000 psi | |
Materion Brush 1915™ Heat Treated Temper Rod, 0.050" - 0.375" Information supplied by Brush Wellman Engineered Materials.Treatment required for max strength: 3.5 hrs @ 370°C or Mill HardenedBrush 1915™ is Brush Wellman's new heat-treatable leaded coppe.. |
|||
Tensile Strength, Yield | >= 480 MPa @Strain 0.200 % |
>= 69600 psi @Strain 0.200 % |
|
Industeel SUPERELSO® 500HR Quenched and Tempered High Strength Steel for Wet H2S Service Description: Superelso® 500 HR (SE 500 HR, "Hydrogen Resistant") is a 500MPa (72ksi) yield strength quenched and tempered steel adapted for pressure equipment operating under sour service conditi.. |
|||
Tensile Strength, Yield | 480 MPa @Strain 0.200 % |
69600 psi @Strain 0.200 % |
|
Haynes 625 alloy, 0% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Tensile Strength, Yield | 480 MPa @Temperature 300 °C |
69600 psi @Temperature 572 °F |
Annealed prior to test |
Special Metals INCOLOY® Alloy MA 956 An iron-chromium-aluminum alloy that is oxide dispersion strengthened and produced by mechanical alloying. Production involves high-energy milling of metal powders to create an alloy with a strengt.. |
|||
Tensile Strength, Yield | 480 MPa | 69600 psi | |
Superior Die Set FORTAL® HR Aluminum Alloy Description: FORTAL is a high strength, lightweight, easy to machine alloy, originally developed to be used in the aerospace industry. It can be found whenever a structure is highly solicited and d.. |
|||
Tensile Strength, Yield | >= 480 MPa @Thickness 16.0 - 35.0 mm |
>= 69600 psi @Thickness 0.630 - 1.38 in |
|
ThyssenKrupp XABO® 500 T Structural Steel This Material Specification applies to thermo mechanically rolled flat products in thicknesses up to 60 mm. The criteria to distinguish the steel grades is the lowest test temperature for the notch-.. |
|||
Tensile Strength, Yield | >= 480 MPa @Thickness 16.0 - 35.0 mm |
>= 69600 psi @Thickness 0.630 - 1.38 in |
|
ThyssenKrupp XABO® 500 Structural Steel This Material Specification applies to thermo mechanically rolled flat products in thicknesses up to 60 mm. The criteria to distinguish the steel grades is the lowest test temperature for the notch-.. |
|||
Tensile Strength, Yield | 480 - 540 MPa @Strain 0.200 % |
69600 - 78300 psi @Strain 0.200 % |
|
CLAL-MSX DECLAFOR® 1015 TD2 Wire quenched/Cold Rolled Copper Alloy Main Characteristic: Age hardening alloyBeriyllium free alloyGood machinabilityHigh mechanical propertiesTypical Applications:Coaxial connectorsSpectacles partsSliding contacts partsAll kind of turn.. |
|||
Tensile Strength, Yield | 480 MPa | 69600 psi | |
Elgiloy® Co-Cr-Ni Alloy, Wire, Heat Treated Heat Treatment 5 hours at 527°C. The strength and hardness values are specific to this heat treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, duc.. |
|||
Tensile Strength, Yield | 480 MPa | 69600 psi | |
ATI Wah Chang TI-45 Nb Applications: Aerospace Rivet Material; High Pressure Oxygenated Gas Vents; Superconducting Wire Information provided by ATI Wah Chang |
|||
Tensile Strength, Yield | 480 - 600 MPa | 69600 - 87000 psi | |
ArcelorMittal FB 590 Hot rolled ferrite-bainite steel Available in the following: uncoated (HDT590F)Description: This range of hot-rolled high strength steels has been developed to meet weight reduction requirements. It comprises four strength levels: .. |
|||
Tensile Strength, Yield | 480 MPa | 69600 psi | ASTM D638 |
Total Lacqrene® 1160(AS) Crystal Polystyrene
(discontinued **) LACQRENE® 1160 is a high resistance, high molecular weight crystal polystyrene mainly for the extrusion industry. It is particularly useful in the production of thick sheet by direct gassing, wher.. |
|||
Tensile Strength, Yield | 480 MPa @Strain 0.200 %, Temperature 540 °C |
69600 psi @Strain 0.200 %, Temperature 1000 °F |
|
Haynes 242® alloy, hot rolled plate, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good thermal.. |
|||
Tensile Strength, Yield | 480 MPa | 69600 psi | |
Elgiloy® Co-Cr-Ni Alloy, Wire The strength and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, ductility, fatigue life, and.. |
|||
Tensile Strength, Yield | 480 - 600 MPa | 69600 - 87000 psi | |
ArcelorMittal FB 590 HHE Hot rolled ferrite-bainite steel Description: This range of hot-rolled high strength steels has been developed to meet weight reduction requirements. It comprises four strength levels: FB 450, 540, 560 and 590. This family of steel.. |