Polymer Property : Tensile Strength, Yield = 620.0 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	4.275 MPa	620.0 psi	-25% change after 70 hours @ 200°C; ASTM D412
Precision Polymer Engineering S65A Silicone Rubber Low Compression Set, Blue Silicone Rubber, 65-75 °IRHD. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain. ASTM & ISO designation = VMQ.Applications: Low compre..
Tensile Strength, Yield	4.275 MPa	620.0 psi	-25% change after 70 hours @ 200°C; ASTM D412
Precision Polymer Engineering S65B Silicone Rubber Low Compression Set, Black Silicone Rubber, 65-75 °IRHD. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain. ASTM & ISO designation = VMQ.Applications: Low compr..
Tensile Strength, Yield	4.275 MPa	620.0 psi	-25% change after 70 hours @ 200°C; ASTM D412
Precision Polymer Engineering S65G Silicone Rubber Low Compression Set, Green Silicone Rubber, 65-75 °IRHD. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain. ASTM & ISO designation = VMQ.Applications: Low compr..
Tensile Strength, Yield	4.275 MPa	620.0 psi	-25% change after 70 hours @ 200°C; ASTM D412
Precision Polymer Engineering S65W Silicone Rubber Low Compression Set, Off-white Silicone Rubber, 65-75 °IRHD. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain. ASTM & ISO designation = VMQ.Applications: Low c..
Tensile Strength, Yield	4.275 MPa	620.0 psi	-25% change after 70 hours @ 200°C; ASTM D412
Precision Polymer Engineering S65Z Silicone Rubber Low Compression Set, Grey Silicone Rubber, 65-75 °IRHD. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain. ASTM & ISO designation = VMQ.Applications: Low compre..