Polymer Property : Tensile Strength, Yield = 445 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English
Tensile Strength, Yield	445 MPa @Strain 0.200 %	64500 psi @Strain 0.200 %
Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1175Â°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095Â°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr..
Tensile Strength, Yield	445 MPa @Strain 0.200 %	64500 psi @Strain 0.200 %
Haynes 188 alloy, plate at RT after 8000 hours at 870Â°C (1600Â°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095Â°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr..
Tensile Strength, Yield	445 MPa @Strain 0.200 %	64500 psi @Strain 0.200 %
Haynes 230Â® alloy, 20% cold reduction, 1177Â°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149Â°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic..
Tensile Strength, Yield	445 MPa @Temperature 760 Â°C	64500 psi @Temperature 1400 Â°F
Haynes HastelloyÂ® W alloy, gas tungsten arc welds, aged 1000 hours at 650Â°C (1200Â°F) Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica..
Tensile Strength, Yield	445 MPa @Strain 0.200 %	64500 psi @Strain 0.200 %
Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1120Â°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095Â°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr..