Polymer Property : Tensile Strength, Yield = 338 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	338 MPa	49000 psi
Kinetics MIM 2.5% SiFe Soft Magnetic Steel Low alloy steel, silicon. A work hardenable steel alloy that offers very good magnetic properties, tensile strength, hardness, wear resistance, and increased spring steel strength. Can be plated or ..
Tensile Strength, Yield	338 MPa @Strain 0.200 %	49000 psi @Strain 0.200 %
Haynes HastelloyÂ® G-30Â® alloy, plate and bar HASTELLOYÂ® G-30Â® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid..
Tensile Strength, Yield	>= 338 MPa	>= 49000 psi
Alcoa UltrAlloy® 6020-T9 Aluminum Weldability = B; Stress Corrosion Cracking Resistance = A; General Corrosion Resistance = B (A = best; E = worst). General 6020 characteristics and uses: Excellent machinability, high corrosion resi..
Tensile Strength, Yield	>= 338 MPa	>= 49000 psi
Alcoa Deltalloy® 4032-T86 Aluminum Weldability = B; Stress Corrosion Cracking Resistance = B; General Corrosion Resistance = C (A = best; E = worst). General 4032 characteristics and uses: Good machinability and drilling characterist..
Tensile Strength, Yield	338 - 400 MPa	49000 - 58000 psi	0.2% offset
Eagle Brass 210 Gilding Metal, Hard CDA 210 is known for its resistance to corrosion. The alloy also lends itself to deep drawing such as bullet jackets and electrical applications where formability and conductivity are required. Typi..
Tensile Strength, Yield	338 - 407 MPa	49000 - 59000 psi	0.2% offset
Eagle Brass 220 Commercial Bronze, 3/4 Hard CDA 220 is known for having very good corrosion resistance, great cold workability and good hot workability for drawing, blanking, coining, stamping, piercing and punching. Typical uses include plum..
Tensile Strength, Yield	338 - 476 MPa	49000 - 69000 psi	0.2% offset
Eagle Brass 735 Nickel Silver 18%, 1/2 Hard 735 is used for coinage, name plates, zippers, flatware, and fashion jewelry.Information provided by Eagle Brass Company
Tensile Strength, Yield	338 MPa @Strain 0.200 %	49000 psi @Strain 0.200 %	Typical; Annealed
ATI Allegheny Ludlum Moly Permalloy Electrical Alloy An alloy with exceptionally high magnetic permeability, very low coercive force, very low core losses, and low reminance by magnetic field annealing. The alloy finds application in magnetic shieldi..
Tensile Strength, Yield	338 MPa @Strain 0.200 %, Temperature 649 °C	49000 psi @Strain 0.200 %, Temperature 1200 °F
Haynes Multimet® alloy, 533.4 by 82.55 mm forging, stress relieved at 649°C (1200°F), air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i..
Tensile Strength, Yield	338 MPa @Strain 0.200 %, Temperature 93.0 °C	49000 psi @Strain 0.200 %, Temperature 199 °F
Haynes Hastelloy® C-22® alloy, 6.4-19.1 mm thick plate, solution heat treated HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al..