Polymer Property : Tensile Strength, Yield = 19300 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	133 - 230 MPa	19300 - 33400 psi	Average value: 173 MPa Grade Count:8
Overview of materials for Polyetherimide (PEI), Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyetherimide, Carbon Fiber Filled". Each property range of values reported is minimum and maximum valu..
Tensile Strength, Yield	133 MPa	19300 psi	Type I, 5 mm/min; ASTM D638
LNP ULTEM® UCF1205 Polyetherimide, 12% Carbon Fiber Reinforcement, 5% PTFE Lubricant (discontinued **) Office equipment internal parts.Features: Lubricated, Good Wear ResistanceForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labe..
Tensile Strength, Yield	133 MPa @Strain 0.200 %, Temperature 982 Â°C	19300 psi @Strain 0.200 %, Temperature 1800 Â°F
Kennametal Stellite StelliteÂ® 6K 1.6 mm thick sheet 13.3 mm^3 volume loss--abrasive wear data. Applications include agitators, augers, ball mills, banbury mills, cams, crusher bearings, dryers, dry presses, dump cars, fans, filters, food machinery, g..
Tensile Strength, Yield	133 MPa	19300 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP Lubricomp OFG26XXP PPS - Linear LNP* Lubricomp* OFG26XXP is a compound based on Linear PPS containing Glass Fiber and Graphite Powder. Characteristics of this grade are Internally Lubricated.This data was supplied by SABIC-IP for..
Tensile Strength, Yield	133 MPa	19300 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP STAT-KON DE004ER PC LNP* STAT-KON* DE004ER is a compound based on Polycarbonate resin containing 20% Carbon Fiber. Added featuresof this material include: Electrically Conductive, Easy Molding, Mold Release.
Tensile Strength, Yield	133 MPa	19300 psi	Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics LNP Stat-kon DEL369E PC LNP* Stat-Kon* DEL369E is a compound based on Polycarbonate containing Carbon Fiber and PTFE. Characteristics of this grade are Flame Retardant and Statically Conductive.This data was supplied by S..
Tensile Strength, Yield	133 MPa	19300 psi	Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics LNP Stat-kon DEL369E PC (Asia Pacific) LNP* Stat-Kon* DEL369E is a Polycarbonate with Carbon Fiber and PTFE. Characteristics of this grade are Flame Retardant.This data was supplied by SABIC-IP for the Asia Pacific region.
Tensile Strength, Yield	133 MPa	19300 psi	ISO 527
SABIC Innovative Plastics LNP STAT-KON REL42 PA 66 LNP* STAT-KON* REL42 is a compound based on Nylon 66 resin containing 20% PTFE, 10% Carbon Fiber. Added features of this material include: Electrically Conductive, Internally Lubricated.
Tensile Strength, Yield	133 MPa	19300 psi	ISO 527
SABIC Innovative Plastics LNP STAT-KON REL42 PA 66 (Asia Pacific) LNP* Stat-kon* REL42 is a compound based on Nylon 66 resin containing PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive, Internally Lubricated.
Tensile Strength, Yield	133 MPa	19300 psi	ASTM D638
Techmer ES HiFillÂ® PES GF20 20% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 20% Filler by WeightInformation provided by TP Composites, Inc.
Tensile Strength, Yield	133 MPa	19300 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP DF0079 PC (Europe-Africa-Middle East) LNP* Thermocomp* DF0079 is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant.
Tensile Strength, Yield	133 MPa	19300 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP OCF62 PPS - Branched LNP* THERMOCOMP* OCF62 is a compound based on PPS-Branched resin containing 10% Carbon Fiber, 30% Glass Fiber. Added feature of this material includes: Easy Molding
Tensile Strength, Yield	133 MPa	19300 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP OCF62E PPS - Branched LNP* THERMOCOMP* OCF62E is a compound based on PPS-Branched resin containing 10% Carbon Fiber, 30% Glass Fiber. Added feature of this material includes: Easy Molding
Tensile Strength, Yield	133 MPa	19300 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP DC0049XF PC LNP* THERMOCOMP* DC0049XF is a compound based on Polycarbonate resin containing 20% Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant.
Tensile Strength, Yield	133 MPa	19300 psi	ASTM D638
Techmer ES HiFillÂ® PES GM20 WT139 20% Milled Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Milled Glass Fiber, 20% Filler by WeightInformation provided by TP Composites, Inc.
Tensile Strength, Yield	133 MPa	19300 psi	Type I, 5 mm/min; ASTM D638
LNP ULTEM® SMU5806 Polyetherimide, 8% Carbon Fiber Reinforcement (discontinued **) Features: Low ShrinkageForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still..