Polymer Property : Tensile Strength, Yield = 113000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	780 MPa @Strain 0.200 %	113000 psi @Strain 0.200 %	Precipitation Hardened. Value at room temperature
Special Metals NIMONICÂ® Alloy 80A A nickel-chromium alloy similar to NIMONIC alloy 75 but made precipitation hardenable by additions of aluminum and titanium. The alloy has good corrosion and oxidation resistance and high tensile a..
Tensile Strength, Yield	780 MPa	113000 psi
SSAB Tunnplat DomexÂ® Wear Steel Sheet DomexÂ® Wear is a new grade of steel sheet in the DomexÂ® range, and its main distinguishing features are good wear resistance, high strength, good bendability, high toughness and good weldabili..
Tensile Strength, Yield	780 MPa @Strain 0.200 %	113000 psi @Strain 0.200 %	Typical
TIMET TIMETAL® 15-3 Titanium Alloy (Ti-15V-3Cr-3Sn-3Al), Anneal Strip/Sheet High-Strength, Cold Formable Strip AlloyIndustry Specifications: USA Aerospace: AMS 4914A.Features: Cold formable and weldable, this strip alloy is primarily used for aircraft ducting, pressure vess..
Tensile Strength, Yield	779 MPa @Strain 0.200 %	113000 psi @Strain 0.200 %
Carpenter Custom Age 625 PLUS® Nickel-Base Alloy, Aged 732°C (1350°F)/8hr/AC Data provided by Carpenter Technology Corporation.Custom Age 625 PLUS® alloy is a precipitation hardenable, nickel-base alloy which, in many environments, displays corrosion resistance similar to t..
Tensile Strength, Yield	780 MPa @Strain 0.200 %	113000 psi @Strain 0.200 %
Haynes 242® alloy, hot rolled plate, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good thermal..
Tensile Strength, Yield	780 MPa @Strain 0.200 %	113000 psi @Strain 0.200 %
Haynes 556® alloy, 20% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Tensile Strength, Yield	780 MPa @Strain 0.200 %	113000 psi @Strain 0.200 %
Haynes 625 alloy, 10% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi..