Polymer Property : Film Tensile Strength at Break, MD = 83.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, MD	83.0 MPa	12000 psi	parallel; ISO 527-3
DSM Akulon® F132 PA6 Film Extrusion, High Viscosity
Film Tensile Strength at Break, MD	83.0 MPa	12000 psi	parallel; ISO 527-3
DSM Akulon® F132-C1 PA6 Film Extrusion, High Viscosity, Lubricated
Film Tensile Strength at Break, MD	83.0 MPa	12000 psi	parallel; ISO 527-3
DSM Akulon® F136 PA6 Very High Viscosity, Film Extrusion
Film Tensile Strength at Break, MD	83.0 MPa	12000 psi	parallel; ISO 527-3
DSM Akulon® F136-C PA6 Film Extrusion, Very High Viscosity, Lubricated
Film Tensile Strength at Break, MD	83.0 MPa	12000 psi	parallel; ISO 527-3
DSM Akulon® F136-C1 PA6 Very High Viscosity, Film Extrusion, Lubricated
Film Tensile Strength at Break, MD	83.0 MPa	12000 psi	parallel; ISO 527-3
DSM Akulon® F234-C PA6 Film Extrusion, High Viscosity, Lubricated