- Polymer Property : Film Tensile Strength at Break, MD = 160 MPa
Polymer Property : Film Tensile Strength at Break, MD = 160 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Break, MD | 160 MPa | 23200 psi | ASTM-D882 |
| Kinlead PL11 Lamination Grade BOPP Plain Film (thickness: 20 µm) PL11 is a general, lamination grade BOPP plain film. It is transparent and non heat sealable. It is excellent for extrusion lamination. One side has corona treatment. It is widely used in laminating.. |
|||
| Film Tensile Strength at Break, MD | 160 MPa | 23200 psi | ASTM-D882 |
| Kinlead PL21 Lamination Grade BOPP Plain Film (thickness: 20 µm) PL21 is a general, lamination grade BOPP plain film. It is transparent and non heat sealable. It is excellent for extrusion lamination. It has excellent dimensional stability, high tensile strength,.. |
|||
| Film Tensile Strength at Break, MD | 160 MPa | 23200 psi | ASTM-D882 |
| Kinlead PM11 Metalizing Grade BOPP Plain Film (thickness: 20 µm) PM11 is a general, metalizing grade BOPP plain film. It is transparent and non heat sealable. It has good heat resistance and tensile strength, and it has excellent metal adhesion. One side has coro.. |
|||
| Film Tensile Strength at Break, MD | 160 MPa | 23200 psi | ASTM-D882 |
| Kinlead PM11 Metalizing Grade BOPP Plain Film (thickness: 30 µm) PM11 is a general, metalizing grade BOPP plain film. It is transparent and non heat sealable. It has good heat resistance and tensile strength, and it has excellent metal adhesion. One side has coro.. |
|||
| Film Tensile Strength at Break, MD | 160 MPa | 23200 psi | ASTM-D882 |
| Kinlead PM11 Metalizing Grade BOPP Plain Film (thickness: 35 µm) PM11 is a general, metalizing grade BOPP plain film. It is transparent and non heat sealable. It has good heat resistance and tensile strength, and it has excellent metal adhesion. One side has coro.. |
|||
| Film Tensile Strength at Break, MD | 160 MPa | 23200 psi | ASTM-D882 |
| Kinlead PP11 Printing Grade BOPP Plain Film (thickness: 20 µm) PP11 is a general, printing grade BOPP plain film. It is transparent and non heat sealable. It has excellent ink adhesion. One side has corona treatment. It is widely used in printing applications.I.. |
|||
| Film Tensile Strength at Break, MD | 160 MPa | 23200 psi | ASTM-D882 |
| Kinlead PP11 Printing Grade BOPP Plain Film (thickness: 30 µm) PP11 is a general, printing grade BOPP plain film. It is transparent and non heat sealable. It has excellent ink adhesion. One side has corona treatment. It is widely used in printing applications.I.. |
|||
| Film Tensile Strength at Break, MD | 160 MPa | 23200 psi | ASTM-D882 |
| Kinlead PP11 Printing Grade BOPP Plain Film (thickness: 40 µm) PP11 is a general, printing grade BOPP plain film. It is transparent and non heat sealable. It has excellent ink adhesion. One side has corona treatment. It is widely used in printing applications.I.. |
|||
| Film Tensile Strength at Break, MD | 160 MPa | 23200 psi | ASTM-D882 |
| Kinlead PT11 Adhesive Tape Grade BOPP Plain Film (thickness: 20 µm) PT11 is a general, adhesive tape grade BOPP plain film. It is transparent and non heat sealable. It has excellent glue adhesion, good dimensional stability, and high tensile strength. One side has c.. |
|||
| Film Tensile Strength at Break, MD | 160 MPa | 23200 psi | ASTM-D882 |
| Kinlead PT11 Adhesive Tape Grade BOPP Plain Film (thickness: 25 µm) PT11 is a general, adhesive tape grade BOPP plain film. It is transparent and non heat sealable. It has excellent glue adhesion, good dimensional stability, and high tensile strength. One side has c.. |
|||
| Film Tensile Strength at Break, MD | 160 MPa | 23200 psi | ASTM-D882 |
| Kinlead PT11 Adhesive Tape Grade BOPP Plain Film (thickness: 28 µm) PT11 is a general, adhesive tape grade BOPP plain film. It is transparent and non heat sealable. It has excellent glue adhesion, good dimensional stability, and high tensile strength. One side has c.. |
|||
| Film Tensile Strength at Break, MD | 160 MPa | 23200 psi | ASTM-D882 |
| Kinlead PT11 Adhesive Tape Grade BOPP Plain Film (thickness: 40 µm) PT11 is a general, adhesive tape grade BOPP plain film. It is transparent and non heat sealable. It has excellent glue adhesion, good dimensional stability, and high tensile strength. One side has c.. |
|||
| Film Tensile Strength at Break, MD | 160 MPa | 23200 psi | ASTM-D882 |
| Kinlead PT12 Adhesive Tape Grade BOPP Plain Film (thickness: 25 µm) PT12 is a super clear, adhesive tape grade BOPP plain film. It is transparent and non heat sealable. It has excellent glue adhesion and high clarity. One side has corona treatment. It is widely used.. |
|||
| Film Tensile Strength at Break, MD | 160 MPa | 23200 psi | ASTM-D882 |
| Kinlead PT12 Adhesive Tape Grade BOPP Plain Film (thickness: 28 µm) PT12 is a super clear, adhesive tape grade BOPP plain film. It is transparent and non heat sealable. It has excellent glue adhesion and high clarity. One side has corona treatment. It is widely used.. |
|||
| Film Tensile Strength at Break, MD | 160 MPa | 23200 psi | ASTM-D882 |
| Kinlead PT12 Adhesive Tape Grade BOPP Plain Film (thickness: 40 µm) PT12 is a super clear, adhesive tape grade BOPP plain film. It is transparent and non heat sealable. It has excellent glue adhesion and high clarity. One side has corona treatment. It is widely used.. |
|||
| Film Tensile Strength at Break, MD | 160 MPa | 23200 psi | ASTM-D882 |
| Kinlead PT21 Adhesive Tape Grade BOPP Plain Film (thickness: 30 µm) PT21 is a general, adhesive tape grade BOPP plain film. It is transparent and non heat sealable. It has excellent glue adhesion. Both sides have corona treatment. It is widely used in industrial adh.. |
|||
| Film Tensile Strength at Break, MD | 160 MPa | 23200 psi | ASTM-D882 |
| Kinlead PT21 Adhesive Tape Grade BOPP Plain Film (thickness: 40 µm) PT21 is a general, adhesive tape grade BOPP plain film. It is transparent and non heat sealable. It has excellent glue adhesion. Both sides have corona treatment. It is widely used in industrial adh.. |
|||
| Film Tensile Strength at Break, MD | 160 MPa | 23200 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| ExxonMobil Bicor™ 20MB666 OPP Film Product Description: Bicor 20MB666 is a biaxially oriented transparent polypropylene film acrylic coated two sides. It provides outstanding performance on all packaging machines and is mainly propos.. |
|||
| Film Tensile Strength at Break, MD | 160 MPa | 23200 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| ExxonMobil Bicor™ 20MB668 OPP Film Product Description: Bicor 20MB668 is a high speed transparent, biaxially oriented polypropylene film, coated one side acrylic, one side very low temperature seal (VLTS) coating. VLTS coating provid.. |
|||
| Film Tensile Strength at Break, MD | 160 MPa | 23200 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| ExxonMobil Bicor™ 21MB777 OPP Film Product Description: Bicor 21MB777 is a high gas barrier, biaxially oriented transparent PP film coated one side PVdC, one side acrylic. This film provides outstanding performance on all packaging m.. |
|||
| Film Tensile Strength at Break, MD | 160 MPa | 23200 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| ExxonMobil Bicor™ 25MB666 OPP Film Product Description: A Biaxially oriented transparent polypropylene film, acrylic coated two sides. It provides outstanding performance on all packaging machines.Availability: Africa & Middle East, .. |
|||
| Film Tensile Strength at Break, MD | 160 MPa | 23200 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| ExxonMobil Bicor™ 25MB668 OPP Film Product Description: A high speed transparent, biaxially oriented polypropylene film, coated one side acrylic, one side very low seal temperature (VLTS) coating. VLTS coating provides excellent perf.. |
|||
| Film Tensile Strength at Break, MD | 160 MPa | 23200 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| ExxonMobil Bicor™ 25MBT666 OPP Film Product Description: Biaxially oriented polypropylene film, acrylic coated two sides. This film is specifically suitable for unsupported overwrapping offering unique aspect and cost reduction advant.. |
|||
| Film Tensile Strength at Break, MD | 160 MPa | 23200 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| ExxonMobil Bicor™ 26MB777 OPP Film Product Description: A high gas barrier, biaxially oriented transparent polypropylene film, coated on one side PVdC, one side acrylic. This film provides outstanding performance on all packaging mac.. |
|||
| Film Tensile Strength at Break, MD | 160 MPa | 23200 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| ExxonMobil Bicor™ 30MB668 OPP Film Product Description: A high speed transparent, biaxially oriented polypropylene film, coated one side very low temperature seal (VLTS) coating. VLTS coating provides excellent performances on high s.. |
|||
| Film Tensile Strength at Break, MD | 160 MPa | 23200 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| ExxonMobil Bicor™ 32MB777 OPP Film Product Description: A high gas barrier, biaxially oriented transparent polypropylene film, coated one side PVdC, one side acrylic. This film provides outstanding performance on all packaging machin.. |
|||
| Film Tensile Strength at Break, MD | 160 MPa | 23200 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| ExxonMobil Bicor™ 30MBT666 OPP Film Product Description: A biaxially oriented transparent polypropylene film, acrylic coated two sides. This film is specifically suitable for unsupported overwrapping, offering unique aspect and cost r.. |
|||
| Film Tensile Strength at Break, MD | 160 MPa | 23200 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| ExxonMobil Bicor™ 20MBT666 OPP Film Product Description: Bicor 20MBT666 is a biaxially oriented transparent polypropylene film acrylic coated two sides. This film is specifically suitable for unprinted overwrapping, offering unique as.. |
|||