Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 297 MPa @Thickness 9.50 - 25.4 mm, Temperature 427 °C |
43100 psi @Thickness 0.374 - 1.00 in, Temperature 801 °F |
0.2% offset |
Haynes Hastelloy® S alloy, flat products Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Tensile Strength, Yield | >= 297 MPa @Strain 0.200 %, Thickness 101.6 - 127 mm |
>= 43100 psi @Strain 0.200 %, Thickness 4.000 - 5.00 in |
Tempers T851/T852 |
Constellium Alumold® 350 Aluminum Alumold-350® has been specifically developed to achieve the best combination of strength at low and high temperatures, together with a good shape stability and machinability. Alumold-350® is parti.. |
|||
Tensile Strength, Yield | 297 MPa @Thickness 3.20 mm, Temperature 316 °C |
43100 psi @Thickness 0.126 in, Temperature 601 °F |
0.2% offset |
Haynes Hastelloy® C-4 alloy, sheet, aged 100 hours at 899°C Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T.. |