Polymer Property : Tensile Strength, Yield = 39000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	269 MPa @Thickness 12.7 mm, Temperature 760 Â°C	39000 psi @Thickness 0.500 in, Temperature 1400 Â°F	0.2% offset
Haynes HastelloyÂ® C-22Â® alloy, transverse, GTAW weldment, sheet - plate HASTELLOYÂ® C-22Â® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an..
Tensile Strength, Yield	269 MPa @Strain 0.200 %, Thickness 6.35 - 12.7 mm	39000 psi @Strain 0.200 %, Thickness 0.250 - 0.499 in
Aleris Alustar H131 Aluminum Alloy Close in composition to AA5059. Used in defense and mining shielding applications for protection against ballistics and blasts.
Tensile Strength, Yield	269 MPa @Strain 0.200 %, Thickness 12.7 - 50.8 mm	39000 psi @Strain 0.200 %, Thickness 0.500 - 2.00 in
Aleris Alustar H131 Aluminum Alloy Close in composition to AA5059. Used in defense and mining shielding applications for protection against ballistics and blasts.
Tensile Strength, Yield	269 MPa @Strain 0.200 %, Thickness 50.83 - 76.2 mm	39000 psi @Strain 0.200 %, Thickness 2.001 - 3.00 in
Aleris Alustar H131 Aluminum Alloy Close in composition to AA5059. Used in defense and mining shielding applications for protection against ballistics and blasts.
Tensile Strength, Yield	269 MPa @Strain 0.200 %, Thickness 6.35 - 12.7 mm	39000 psi @Strain 0.200 %, Thickness 0.250 - 0.499 in
Aleris Alustar H136 Aluminum Alloy Close in composition to AA5059. Used in defense and mining shielding applications for protection against ballistics and blasts. H136 has a higher elongation than H131 and so provides better protec..
Tensile Strength, Yield	269 MPa @Strain 0.200 %, Thickness 12.7 - 50.8 mm	39000 psi @Strain 0.200 %, Thickness 0.500 - 2.00 in
Aleris Alustar H136 Aluminum Alloy Close in composition to AA5059. Used in defense and mining shielding applications for protection against ballistics and blasts. H136 has a higher elongation than H131 and so provides better protec..
Tensile Strength, Yield	269 MPa @Strain 0.200 %, Thickness 50.83 - 76.2 mm	39000 psi @Strain 0.200 %, Thickness 2.001 - 3.00 in
Aleris Alustar H136 Aluminum Alloy Close in composition to AA5059. Used in defense and mining shielding applications for protection against ballistics and blasts. H136 has a higher elongation than H131 and so provides better protec..
Tensile Strength, Yield	269 MPa @Thickness 6.35 mm, Temperature 538 °C	39000 psi @Thickness 0.250 in, Temperature 1000 °F	0.2% offset
Haynes Hastelloy® C-22® alloy, transverse, GTAW short arc weldment, plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al..
Tensile Strength, Yield	269 MPa @Thickness 12.7 mm, Temperature 760 °C	39000 psi @Thickness 0.500 in, Temperature 1400 °F	0.2% offset
Haynes Hastelloy® C-22® alloy, transverse, GTAW short arc weldment, plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al..