Polymer Property : Tensile Strength, Yield = 16800 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	116 MPa @Strain 1.00 %, Temperature 400 °C	16800 psi @Strain 1.00 %, Temperature 752 °F	EN min.; EN 10002-5
Outokumpu 4306 Cr-Ni Austenitic Stainless Steel General purpose steel with good corrosion resistance.Applications: Wide variety of applications in construction, chemical, petroleum, automobile, and domestic appliance markets.Available in hot roll..
Tensile Strength, Yield	116 MPa @Strain 1.00 %, Temperature 400 °C	16800 psi @Strain 1.00 %, Temperature 752 °F	EN min.; EN 10002-5
Outokumpu 4307 Cr-Ni Austenitic Stainless Steel General purpose steel with good corrosion resistance.Applications: Wide variety of applications in construction, chemical, petroleum, automobile, and domestic appliance markets.Available in hot roll..
Tensile Strength, Yield	116 MPa @Strain 0.200 %, Temperature 200 °C	16800 psi @Strain 0.200 %, Temperature 392 °F	EN min.; EN 10002-5
Outokumpu 4828 High Temperature Austenitic Stainless Steel Standardized high temperature steel for service at temperatures of up to 950-1000°C in dry air. Utilization in the temperature range of 600-900°C can lead to embrittlement.Applications: Heat and ..
Tensile Strength, Yield	116 MPa @Strain 0.200 %, Temperature 200 °C	16800 psi @Strain 0.200 %, Temperature 392 °F	EN min.; EN 10002-5
Outokumpu 4833 High Temperature Austenitic Stainless Steel Standardized high temperature steel for service at temperatures of up to 950-1000°C in dry air. Utilization in the temperature range of 600-900°C can lead to embrittlement.Applications: Heat and ..
Tensile Strength, Yield	116 MPa @Strain 0.200 %, Temperature 200 °C	16800 psi @Strain 0.200 %, Temperature 392 °F	EN min.; EN 10002-5
Outokumpu 4845 High Temperature Austenitic Stainless Steel Standardized high-temperature steel for use at temperatures up to 1100°C in dry air. Prone to embrittlement after exposure between 600-900°C. Applications: Heat and creep resistance. For use o..