Polymer Property : Tensile Strength, Yield = 108000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	745 MPa @Temperature -53.9 °C	108000 psi @Temperature -65.0 °F	0° Direction, Dry; ASTM D638
Park Electrochemical Nelcote® E-761 Epoxy Prepreg, 4581 Quartz Nelcote® E-761 is a versatile self-adhesive epoxy matrix for use in aerospace and commercial application where ease of processing and cost are key considerations.Key Features and Benefits:Controlle..
Tensile Strength, Yield	746 MPa @Strain 0.200 %, Thickness 12.7 mm	108000 psi @Strain 0.200 %, Thickness 0.500 in
Haynes HastelloyÂ® S alloy, flat products, solution heat-treated at 538Â°C (1000Â°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Tensile Strength, Yield	744 MPa @Strain 0.200 %, Thickness 3.20 mm	108000 psi @Strain 0.200 %, Thickness 0.126 in	Welded then age-hardened
Haynes HastelloyÂ® C-22HSâ„¢ Nickel Alloy Gas Tungsten Arc Welded (GTAW) Sheet Outstanding Corrosion Resistance, High Strength HASTELLOYÂ® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou..
Tensile Strength, Yield	747 MPa @Treatment Temp. 427 Â°C, Time 3.60e+6 sec	108000 psi @Treatment Temp. 801 Â°F, Time 1000 hour	0.2%. Room temp test after thermal exposure
Haynes HastelloyÂ® C-22HSâ„¢ Nickel Alloy Plate, Age-hardened Outstanding Corrosion Resistance, High Strength HASTELLOYÂ® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou..
Tensile Strength, Yield	742 MPa @Strain 0.200 %	108000 psi @Strain 0.200 %	No thermal exposure
Haynes HastelloyÂ® C-22HSâ„¢ Nickel Alloy Plate, Age-hardened Outstanding Corrosion Resistance, High Strength HASTELLOYÂ® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou..
Tensile Strength, Yield	745 MPa @Temperature -55.0 °C	108000 psi @Temperature -67.0 °F	Dry
Hexcel® HexPly® F522 Epoxy Resin, W3C282 Carbon Fabric Hexcel designation: TW3C282-42"-F522; Fiber: Toho® G30/500-3KInformation provided by HexCel
Tensile Strength, Yield	744 MPa @Temperature 23.0 °C	108000 psi @Temperature 73.4 °F	T300; Fill Tension; (AMB)
Hexcel® HexPly® M65 Bismaleimide Resin, Carbon Fabric Form Fibers: T300-3K, AS4C-3KInformation provided by HexCel