Polymer Property : Tensile Strength, Yield = 105000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	>= 724 MPa @Strain 0.200 %	>= 105000 psi @Strain 0.200 %	H1150 Condition - 620Â°C at 4 hr
Latrobe LescalloyÂ® 17-4 VAC-ARC Precipitation Hardening Stainless Steel LESCALLOY 17-4 VAC-ARC steel is a precipitation hardening martensitic stainless steel. A wide range of mechanical properties is available via simple aging within a 900-1150Â°F (482-621Â°C) tempe..
Tensile Strength, Yield	724 MPa @Strain 0.200 %	105000 psi @Strain 0.200 %	5.25 in. Test Specimen
Latrobe LescalloyÂ® 410Cb High Strength Stainless Steel LESCALLOY 17-4 VAC-ARC steel is a precipitation hardening martensitic stainless steel. A wide range of mechanical properties is available via simple aging within a 900-1150Â°F (482-621Â°C) tempe..
Tensile Strength, Yield	727 MPa @Strain 0.200 %, Diameter 12.7 mm	105000 psi @Strain 0.200 %, Diameter 0.500 in	As Welded and Aged at 1850Â°F(1010Â°C)/2hr/AC + 1450Â°F(788Â°C)/8h/AC
Haynes 282Â® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform Excellent High Temperature Strength HAYNESÂ® 282Â® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la..
Tensile Strength, Yield	724 MPa @Strain 0.200 %, Thickness <=38.1 mm	105000 psi @Strain 0.200 %, Thickness <=1.50 in	Tension
Crucible Steel Aquamet® 19 Stainless Steel AQUAMET 19 is a modified Type 304 stainless steel that is fully austenitic and non-magnetic. Strengthened by adding nitrogen to the melt, it has better corrosion resistance than Type 304 stainless. ..
Tensile Strength, Yield	721 MPa @Strain 0.200 %	105000 psi @Strain 0.200 %	50% Cold Worked
AK Steel 409 ULTRA FORM® Stainless Steel AK Steel 409 ULTRA FORM Stainless Steel provides an outstanding combination of improved forming and welding characteristics, while providing superior resistance to oxidation, corrosion, ridging and ..
Tensile Strength, Yield	>= 724 MPa @Strain 0.200 %	>= 105000 psi @Strain 0.200 %	AMS 5542 aged, sheet
ATI Allegheny Ludlum Altemp® X-750 Nickel-Based superalloy Characteristics: precipitation hardenable, high strength up to 1300°F, oxidation resistant up to 1800°F. Applications: aerospace, heat treatment fixtures, forming tools, extrusion dies.Information..
Tensile Strength, Yield	>= 724 MPa @Strain 0.200 %	>= 105000 psi @Strain 0.200 %	AMS 5598 aged, plate
ATI Allegheny Ludlum Altemp® X-750 Nickel-Based superalloy Characteristics: precipitation hardenable, high strength up to 1300°F, oxidation resistant up to 1800°F. Applications: aerospace, heat treatment fixtures, forming tools, extrusion dies.Information..