Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | >= 621 MPa @Thickness 25.4 - 50.8 mm |
>= 90000 psi @Thickness 1.00 - 2.00 in |
|
Cadi 1 MOLD-MOR™ A very hard heat treatable copper alloy with moderate electrical conductivity. C18000 offers excellent value for the properties it offers. C18000 is a viable substitute for C17500 and C17510 for m.. |
|||
Tensile Strength at Break | >= 621 MPa @Thickness 25.4 - 50.8 mm |
>= 90000 psi @Thickness 1.00 - 2.00 in |
|
Cadi 10 MOLD-MOR™ A Copper Nickel Silicon Chromium Alloy with high thermal conductivity and moderate hardness.Information provided by Cadi Company. |
|||
Tensile Strength at Break | >= 621 MPa @Thickness 25.4 - 50.8 mm |
>= 90000 psi @Thickness 1.00 - 2.00 in |
|
Cadi 2 MOLD-MOR™ A very hard heat treatable beryllium-copper alloy with moderate electrical conductivity. C17510 can be utilized when a combination of very good mechanical strength along with moderate electrical an.. |
|||
Tensile Strength at Break | >= 621 MPa @Thickness 25.4 - 50.8 mm |
>= 90000 psi @Thickness 1.00 - 2.00 in |
|
Cadi 20 MOLD-MOR™ A Beryllium Copper Alloy with high thermal conductivity and moderate hardness.Information provided by Cadi Company. |
|||
Tensile Strength at Break | >= 621 MPa @Thickness 25.4 - 50.8 mm |
>= 90000 psi @Thickness 1.00 - 2.00 in |
|
Cadi C17500 Copper Alloy Information provided by Cadi Company. |