Polymer Property : Tensile Strength at Break = 3130 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	21.6 MPa @Temperature 100 Â°C, Time 259000 sec	3130 psi @Temperature 212 Â°F, Time 72.0 hour	Circulating Oven Aging
LG Chemical NBR 7030 High Acrylonitrile Polymer Description: NBR 7030 is a mechanically fully-fluxed polyblend of 70 parts medium-high acrylonitrile rubber and 30 parts polyvinylchloride resin. Since NBR 7030 are prefluxed, normal temperature for..
Tensile Strength at Break	21.6 MPa @Treatment Temp. 100 Â°C, Time 259000 sec	3130 psi @Treatment Temp. 212 Â°F, Time 72.0 hour	Aged ASTM D #3 Oil
LG Chemical NBR 7030 High Acrylonitrile Polymer Description: NBR 7030 is a mechanically fully-fluxed polyblend of 70 parts medium-high acrylonitrile rubber and 30 parts polyvinylchloride resin. Since NBR 7030 are prefluxed, normal temperature for..
Tensile Strength at Break	21.6 MPa @Treatment Temp. 100 Â°C, Time 259000 sec	3130 psi @Treatment Temp. 212 Â°F, Time 72.0 hour	Aged ASTM D #3 Oil
LG Chemical NBR 6280 High Acrylonitrile Polymer Description: NBR 6280 is a copolymer of butadiene and acrylonitrile manufactured by advanced emulsion polymerization technology of Goodyear and LG Chem. NBR 6280 is a non staining, high mooney, and ..