Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 33.8 MPa | 4900 psi | 2 in/min; ASTM D638 |
RheTech Products T20P100-01EG 20% Talc Reinforced Polypropylene, General Purpose Black, Extrusion Grade Applications: Consumer goodsAutomotive componentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 33.8 MPa | 4900 psi | after 16 hours in 50°C water |
Malvern Minerals Thermoplastic Polyester with Novacite® 1250 Quartz Filler Product data demonstrates the effect of the Novacite (untreated lamellar quartz) filler. A separate entry demonstrates the effect of surface-treated Novakup filler in thermoplastic polyester Th.. |
|||
Tensile Strength at Break | 33.8 MPa | 4900 psi | ASTM D638 |
Techmer ES Plastiblend® ABS GN005 Availability: North AmericaForms: PelletsFeatures: General PurposeAppearance: GreenInformation provided by TP Composites, Inc. |
|||
Tensile Strength at Break | 33.8 MPa | 4900 psi | ASTM D638 |
Techmer ES Plastiblend® ABS NAT Availability: North AmericaForms: PelletsFeatures: General PurposeAppearance: Natural ColorInformation provided by TP Composites, Inc. |
|||
Tensile Strength at Break | 33.8 MPa | 4900 psi | ASTM D638 |
Techmer ES Plastiblend® ABS 92RK Availability: North AmericaForms: PelletsFeatures: General PurposeProcessing Method: Injection MoldingInformation provided by TP Composites, Inc. |
|||
Tensile Strength at Break | 33.8 MPa | 4900 psi | ASTM D638 |
Techmer ES Plastiblend® ABS LE BK Availability: North AmericaForms: PelletsFeatures: Low ExtractablesAppearance: BlackInformation provided by TP Composites, Inc. |
|||
Tensile Strength at Break | 33.8 MPa | 4900 psi | ASTM D638 |
Plastics Group Polifil® T-40 40% Talc-Reinforced Polypropylene Polifil® T series compounds are homopolymer polypropylene resins reinforced with asbestos-free talc. They possess high flex modulus, high deflection temperature, good chemical resistance and colora.. |
|||
Tensile Strength at Break | 33.8 MPa | 4900 psi | ASTM D638 |
Chase Plastics CP Pryme® NN200STL (COND, 50% RH) Nylon 66, Super-Toughened, Internally Lubricated Information provided by Chase Plastics. |
|||
Tensile Strength at Break | 33.8 MPa | 4900 psi | Molded and tested in accordance with ASTM D4976; ASTM D638 |
Dow UNIVAL™ DMDA-6320 NT 7 High Density Polyethylene Resin (HDPE) Low swell Complies with U.S. FDA 21 CFR 177.1520 (c) 3.2a UNIVAL™ DMDA-6320 NT 7 is a multipurpose polymer designed for the high speed production of blow molded containers used to package household.. |
|||
Tensile Strength at Break | 33.8 MPa | 4900 psi | Molded and tested in accordance with ASTM D4976; ASTM D638 |
Dow UNIVAL™ DMDD-6230 NT 7 High Density Polyethylene Resin (HDPE) Good extrusion characteristics Complies with U.S. FDA 21 CFR 177.1520 (c) 3.2a UNIVAL™ DMDD-6230 NT 7 is specifically designed for use in either intermittent or continuous blow molding equipment to.. |
|||
Tensile Strength at Break | 33.8 MPa | 4900 psi | ASTM D412 |
3M Scotchcast™ 4 Electrical Insulating Resin 3M Scotchcast Electrical Insulating Resin 4 is a two-part, epoxy insulating and encapsulating resin. This resin, mixed in its unique two-part bag, generates its own heat to cure. Its compatibility w.. |
|||
Tensile Strength at Break | 33.8 MPa | 4900 psi | ASTM D638 |
Techmer ES Plastiblend® ABS 8008 Availability: North AmericaForms: PelletsFeatures: General Purpose Appearance: Natural ColorInformation provided by TP Composites, Inc. |
|||
Tensile Strength at Break | 33.8 MPa | 4900 psi | ASTM D638 |
Resirene Resirene® HF-555 General Purpose Polystyrene Features:Very High FlowEasy ProcessingHigh ProductivityFDA Rating: 21 CFR 177.1640External Lubrication AvailableApplications:Thin Wall ApplicationsInjectionHard to Fill MoldsDisposablesCosmetics Cas.. |