Polymer Property : Tensile Strength at Break = 31800 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	219 MPa	31800 psi	ASTM D638
Polymer Resources NY66-G50 Nylon 66, 50% Glass Reinforced Nylon 66, 50% Glass Reinforced, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are test..
Tensile Strength at Break	219 MPa	31800 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP RFN18SXS PA 66 (Europe-Africa-Middle East) LNP* Lubricomp* RFN18SXS is a compound based on Nylon 66 resin containing Glass Fiber, MOS2. Added features of this material include: Heat Stabilized.
Tensile Strength at Break	219 MPa	31800 psi	ASTM D638
SABIC Innovative Plastics LNP STAT-KON RE004 PA 66 LNP* STAT-KON* RE004 is a compound based on Nylon 66 resin containing 20% Carbon Fiber. Added features of this material include: Electrically Conductive.
Tensile Strength at Break	219 MPa	31800 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP EC006 PEI (Europe-Africa-Middle East) LNP* THERMOCOMP* EC006 is a compound based on Polyetherimide resin containing Carbon Fiber. Added features include: Electrically Conductive.
Tensile Strength at Break	219 MPa	31800 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP LC006 PEEK (Europe-Africa-Middle East) LNP* THERMOCOMP* LC006 is a compound based on Polyetheretherketone containing Carbon Fiber. Added features include: Electrically Conductive.
Tensile Strength at Break	219 MPa	31800 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP VERTON RV00AE PA 66 LNP* VERTON* RV00AE is a compound based on Nylon 66 containing 50% Long Glass Fiber. Added features of this grade include: Easy Molding, Structural.