Polymer Property : Tensile Strength at Break = 2370 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	16.3 MPa	2370 psi	2 in/min; ASTM D638
Ineos N01G-02 Polypropylene Impact Copolymer N01G-02 is a low melt flow rate polypropylene impact copolymer designed for blow molding, extrusion, and compounding applications. The grade benefits from a very high impact resistance at room and l..
Tensile Strength at Break	16.3 MPa	2370 psi	Press Cure 5 minutes @ 177°C, Post Cure 24 hours @ 260°C
3M Dyneon™ FE 5640Q Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FE 5640Q can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formu..
Tensile Strength at Break	16.3 MPa	2370 psi	Press Cure 5 minutes @ 177°C, Post Cure 24 hours @ 260°C
3M Dyneon™ FC 2180 Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FC 2180 can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formul..