Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 237 MPa | 34400 psi | ISO 527 |
Nilit FRIANYL A63 CV30 Nylon 6.6 for injection molding, 30% carbon fiber reinforced Nylon 6.6 for injection molding (good conductive and electrostatic properties).Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Tensile Strength at Break | 237 MPa | 34400 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP QC008 PA6.10 LNP* THERMOCOMP* QC008 is a compound based on Nylon 6/10 containing 40% Carbon Fiber. Added feature of this grade is: Electrically Conductive. |
|||
Tensile Strength at Break | 237 MPa | 34400 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP RX98372H PA 66 (Asia Pacific) LNP* Thermocomp* RX98372H is a compound based on Nylon 66 resin containing Glass Fiber. |