Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 19.2 MPa | 2780 psi | 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible 90039 Polyvinyl Chloride, Flexible (PVC, Flexible) Automotive OEM approval(s).Information provided by PolyOne |
|||
Tensile Strength at Break | 19.2 MPa | 2780 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible 90049 Polyvinyl Chloride, Flexible (PVC, Flexible) Automotive OEM approval(s).Information provided by PolyOne |
|||
Tensile Strength at Break | 19.2 MPa @Temperature 200 °C, Time 1.21e+6 sec |
2790 psi @Temperature 392 °F, Time 336 hour |
After Dry Heat Aging; ASTM D865 |
Seals Eastern 7182D Fluorocarbon-Elastomer Formulated AFLAS® high-temperature "sour" oil & gas service. Excellent acid and base resistance.Information provided by Seals Eastern, Inc. |
|||
Tensile Strength at Break | 19.2 MPa | 2780 psi | ISO R 527 |
Stir SpA AF 95 CZ (PVC) Application: Extrusion flame resistant sheath CEI 20-11 type R 2Information provided by STIR SpA |
|||
Tensile Strength at Break | 19.2 MPa | 2780 psi | ASTM D638 |
Teknor Apex APEX® 89-P129A-NT Polyvinyl Chloride, Flexible Notes: RoHS Compliant Features: High Heat Resistant; Low to no Migration; Oil Resistant Uses: Flexible Cord Jacketing Agency Ratings: UL 62 Forms: PelletsInformation Provided by Teknor Apex |