Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 12.8 MPa | 1860 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible 90054 Polyvinyl Chloride, Flexible (PVC, Flexible) Automotive OEM approval(s).Information provided by PolyOne |
|||
Tensile Strength at Break | 12.8 MPa | 1860 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible 90215 Polyvinyl Chloride, Flexible (PVC, Flexible) Provisional Product Information - Physical and Mechanical properties based on initial production.Information provided by PolyOne |
|||
Tensile Strength at Break | 12.8 MPa | 1860 psi | 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible FC801 Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength at Break | 12.8 MPa | 1860 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible 90037 Polyvinyl Chloride, Flexible (PVC, Flexible) Automotive OEM approval(s).Information provided by PolyOne |
|||
Tensile Strength at Break | 12.8 MPa | 1860 psi | ISO R 527 |
Stir SpA Z 65 AT S (PVC) Application: Molding for beach footwearInformation provided by STIR SpA |
|||
Tensile Strength at Break | 12.8 MPa | 1860 psi | ASTM D412 |
Teknor Apex Telcar® TL-340-S Thermoplastic Elastomer Uses: Automotive Applications; Automotive Exterior Parts; Automotive Exterior Trim; Automotive Interior Parts; Blow Molding Applications; General Purpose; Grommets; Weatherstripping Forms: Pellets .. |
|||
Tensile Strength at Break | 12.8 MPa | 1860 psi | after aging, 168h, 165°C |
Borealis FR4830 Chemically Crosslinkable Polyethylene Compound for Primary Automotive Wires FR4830 is a chemically crosslinkable Non-halogen flame retardant Polyethylene compound for Primary Automotive and Appliance Wire. Applications: FR4830 is intended for use as a 125º C rated primary .. |
|||
Tensile Strength at Break | 12.8 MPa | 1860 psi | after aging, 168h, 165°C |
Borealis FR4837 Chemically Crosslinkable Polyethylene Compound for Primary Automotive Wires FR4837 is a chemically crosslinkable Non-halogen flame retardant Polyethylene compound for Primary Automotive and Appliance Wire. Applications: FR4837 is intended for use as a 125º C rated primary.. |
|||
Tensile Strength at Break | 12.8 MPa | 1860 psi | |
Daikin DAI-EL G-555 Fluoroelastomer Terpolymer, Bisphenol Curable Grade, 69% Fluorine Content Offers minimal compression set and excellent sealing. The terpolymer type is able to withstand polarized solvents to realize a wide range of application.Features: Products with excellent balance of.. |
|||
Tensile Strength at Break | 12.8 MPa | 1860 psi | ASTM D882 |
3M Scotch-Weld™ DP100 Plus Clear Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP100 Plus Clear is a fast setting, two-part, 1:1 mix ratio mercaptan-cured epoxy adhesive. It is a unique among fast setting mercaptan cure epoxies in that it comb.. |