Polymer Property : Tensile Strength at Break = 13400 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	92.4 MPa	13400 psi	ASTM D638
Ravago Manufacturing Americas Echo® RPC40G BK Polypropylene Homopolymer Available in North America Filler: Glass Fiber Reinforcement, 40% Filler by weight Recycled Content: YesFeatures: Homopolymer Color: Black Form: Pellets Information provided by Ravago
Tensile Strength at Break	92.2 MPa	13400 psi	ASTM D638
Mitsui AURUM® 450 Thermoplastic Polyimide Resin, Non-filled (discontinued **) AURUM® is an easy melt, processable and recyclable thermoplastic polyimide resin that provides continuous service temperatures to 465° F in its amorphous state and up to 550° F when annealed to i..
Tensile Strength at Break	92.5 MPa @Temperature 160 - 175 °C, Time 1.80e+7 sec	13400 psi @Temperature 320 - 347 °F, Time 5000 hour	5 [mm/min], 50% Loss of Tensile Strength; ICE 216
Akro-Plastic Akromid® A3 GF 25 (2420) PA 6.6 Dry, 25% Glass Filled AKROMID® A (Polyamide 6.6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperat..
Tensile Strength at Break	92.5 MPa @Temperature 130 - 150 °C, Time 7.20e+7 sec	13400 psi @Temperature 266 - 302 °F, Time 20000 hour	5 [mm/min], 50% Loss of Tensile Strength; ICE 216
Akro-Plastic Akromid® A3 GF 25 (2420) PA 6.6 Dry, 25% Glass Filled AKROMID® A (Polyamide 6.6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperat..
Tensile Strength at Break	92.5 MPa @Temperature 160 - 175 °C, Time 1.80e+7 sec	13400 psi @Temperature 320 - 347 °F, Time 5000 hour	5 [mm/min], 50% Loss of Tensile Strength; ISO 527-1/2
Akro-Plastic Akromid® B3 GF 30 (2472) PA 6 Dry, 30% Glass Filled AKROMID® B (Polyamide 6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperatur..
Tensile Strength at Break	92.5 MPa @Temperature 130 - 150 °C, Time 7.20e+7 sec	13400 psi @Temperature 266 - 302 °F, Time 20000 hour	5 [mm/min], 50% Loss of Tensile Strength; ISO 527-1/2
Akro-Plastic Akromid® B3 GF 30 (2472) PA 6 Dry, 30% Glass Filled AKROMID® B (Polyamide 6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperatur..