Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 81.4 MPa | 11800 psi | ASTM D638 |
PolyOne Stat-Tech™ ST9620-0020 ES Red Liquid Crystal Polymer + PPS (LCP+PPS) Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compound.. |
|||
Tensile Strength at Break | 81.4 MPa | 11800 psi | ASTM D638 |
Ravago Manufacturing Americas Hylon® N1020MHL Nylon 6/6
(discontinued **) Available in North America Filler: Mineral, 20% Filler by WeightAdditive: Heat Stabilizer and Lubricant Features: Lubricated and Heat StabilizedForm: Pellets Processing Method: Injection MoldingIn.. |
|||
Tensile Strength at Break | 81.4 MPa | 11800 psi | ASTM D638 |
Firestone CLM200-001 Nylon 6 Used for monofiliament extrusion. Natural color. Not heat stabilized or modified. Lubricated. Chip size is 2 x 3.5 mm.Information provided by Firestone |
|||
Tensile Strength at Break | 81.4 MPa @Thickness 3.20 mm |
11800 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
LG Chemical Lupox® TE5100 PBT+PC+GF10% Description: Injection Molding, PBT+PC+GF10%, High Impact resistant, Dimensional StabilityApplication: Automotive (Bumper Back Beam)CAS No. 30965-26-5, 103598-77-2 and 65997-17-3Information provided.. |
|||
Tensile Strength at Break | 81.4 MPa | 11800 psi | ASTM D638 |
Plastics Group Polifil® 628L Nylon 6/6 (DAM) Polifil® NYLON 6/6 combines good abrasion and chemical resistance.Applications: ValvesBearingsBearing casesStandard processing techniques are applicable. Information provided by The Plastics Group... |
|||
Tensile Strength at Break | 81.4 MPa | 11800 psi | ASTM D638 |
Chase Plastics CP Pryme® N333GL (COND, 50% RH) Nylon 6 (Utility Grade), 33% Glass Fiber Reinforced, Internally Lubricated Information provided by Chase Plastics. |
|||
Tensile Strength at Break | 81.4 MPa | 11800 psi | ASTM D638 |
Plastics Group Polifil® GFPPCC-20 20% Glass Reinforced Polypropylene Polifil® GFPPCC series compounds are homopolymer polypropylenes reinforced with chemically coupled glass fibers. These compounds offer superior strength and stiffness, improved elevated temperature.. |