Polymer Property : Tensile Strength at Break = 1.86 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	1.86 MPa	270 psi	After oven air again 168 hrs. @ 150°C; ASTM D412
Advanced Elastomer Systems Santoprene® 8281-35W237 Thermoplastic Rubber (discontinued **) Description: A colorable thermoplastic medical grade elastomer. It has USP Class VI Certificate of Compliance for biocompatibility and can be processed using injection molding, extrusion, or other ..
Tensile Strength at Break	1.86 MPa	270 psi
Taiwan PU Corporation CPU-69-A/B Mixing Ratio 100/26 Polyurethane Casting Elastomer Compound of CPU-69-A/B with a mixing ratio of 100/26.Information provided by Taiwan PU Corporation.MatWeb has a separate entry for the unmixed A nd B components.
Tensile Strength at Break	1.86 MPa	270 psi	ASTM D638
ExxonMobil HDPE HD 6719.17 High Density Polyethylene Copolymer Resin Product Description: HD 6719 is a narrow molecular weight hexane copolymer designed for a wide rage of injection molding applications, combining easy processability with good toughness properties. I..
Tensile Strength at Break	1.86 MPa	270 psi	ASTM D638
ExxonMobil HDPE HD 6719.62 High Density Polyethylene Copolymer Resin Product Description: HD 6719 is a narrow molecular weight hexane copolymer designed for a wide rage of injection molding applications, combining easy processability with good toughness properties. I..
Tensile Strength at Break	1.86 MPa	270 psi
Abatron AboSeal 8104-15 Polysulfide, Thixotropic or Self-Leveling Sealant and Caulk AboSeal 8104-15 is a 2-part, 100% solids, thixotropic or self-leveling polysufide. It comes in brown, black, and other dark colors. It is preferred to 8104-14 where elongation and color are more imp..
Tensile Strength at Break	1.86 MPa @Temperature 60.0 °C, Time 1.04e+6 sec	270 psi @Temperature 140 °F, Time 288 hour	JRF
3M AC-730 Class B-12 Aerospace Sealant 3M Aerospace Sealant AC-730 Class B are fast cure, two-part, manganese-cured, non-chromate containing corrosion inhabiting sealants. These Sealants provide an effective barrier against the common ca..
Tensile Strength at Break	1.86 MPa @Temperature 60.0 °C, Time 1.04e+6 sec	270 psi @Temperature 140 °F, Time 288 hour	JRF
3M AC-730 Class B-2 Aerospace Sealant 3M Aerospace Sealant AC-730 Class B are fast cure, two-part, manganese-cured, non-chromate containing corrosion inhabiting sealants. These Sealants provide an effective barrier against the common ca..
Tensile Strength at Break	1.86 MPa @Temperature 60.0 °C, Time 1.04e+6 sec	270 psi @Temperature 140 °F, Time 288 hour	JRF
3M AC-730 Class B-6 Aerospace Sealant 3M Aerospace Sealant AC-730 Class B are fast cure, two-part, manganese-cured, non-chromate containing corrosion inhabiting sealants. These Sealants provide an effective barrier against the common ca..
Tensile Strength at Break	1.86 MPa @Thickness 3070 mm, Temperature 168 °C	270 psi @Thickness 121 in, Temperature 334 °F	MIL-PRF-81733 AND AS5127A
3M AC-736 B-2 Aerospace Sealant 3M Aerospace Sealant AC-736 B-2 is a non-chromate corrosion inhabiting sealants, fast cure, low density two-component, manganese dioxide cure, polysulfide fuselage sealant. These Sealants act as an ..
Tensile Strength at Break	1.86 MPa @Treatment Temp. 121 °C, Time 605000 sec	270 psi @Treatment Temp. 250 °F, Time 168 hour	MIL-PRF-81733 AND AS5127A
3M AC-736 B-2 Aerospace Sealant 3M Aerospace Sealant AC-736 B-2 is a non-chromate corrosion inhabiting sealants, fast cure, low density two-component, manganese dioxide cure, polysulfide fuselage sealant. These Sealants act as an ..
Tensile Strength at Break	1.86 MPa	270 psi	ASTM D412
3M SJ6512 Protective Product, Molded Shapes 3M Bumpon Protective Products Quite Clear SJ6500 Series are molded cushioning products that utilize a special, soft polyurethane formulation and synthetic rubber adhesive system. This unique constru..
Tensile Strength at Break	1.86 MPa	270 psi	ASTM D412
3M SJ6553 Protective Product, Molded Shapes 3M Bumpon Protective Products Quite Clear SJ6500 Series are molded cushioning products that utilize a special, soft polyurethane formulation and synthetic rubber adhesive system. This unique constru..
Tensile Strength at Break	1.86 MPa	270 psi	ASTM D412
3M SJ6506 Protective Product, Molded Shapes 3M Bumpon Protective Products Quite Clear SJ6500 Series are molded cushioning products that utilize a special, soft polyurethane formulation and synthetic rubber adhesive system. This unique constru..
Tensile Strength at Break	1.86 MPa	270 psi	ASTM D412
3M SJ6561 Protective Product, Molded Shapes 3M Bumpon Protective Products Quite Clear SJ6500 Series are molded cushioning products that utilize a special, soft polyurethane formulation and synthetic rubber adhesive system. This unique constru..
Tensile Strength at Break	1.86 MPa	270 psi	ASTM D 412
CPT C-Flex® R70-190 Opaque Biocompatible TPE C-Flex® is a family of patented thermoplastic elastomers which range in hardness from 5 shore A to 95 shore A. C-Flex® TPE's are biocompatible polymer blends which meet or exceed the current..
Tensile Strength at Break	1.86 MPa @Temperature 60.0 °C, Time 1.04e+6 sec	270 psi @Temperature 140 °F, Time 288 hour	JRF
3M AC-730 Class B-1/2 Aerospace Sealant 3M Aerospace Sealant AC-730 Class B are fast cure, two-part, manganese-cured, non-chromate containing corrosion inhabiting sealants. These Sealants provide an effective barrier against the common ca..