Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 0.415 MPa | 60.2 psi | Dynamic, 1 in.<sup>2</sup> (6.45 cm<sup>2</sup>) overlap Jaw Speed 0.5 in./min (12.7 mm/min.); ASTM D-897 |
3M 4462B Double Coated Polyethylene Foam Tape 3M™ Double Coated Polyethylene Foam Tapes 4462W, 4462B, 4466W and 4466B combine a conformable closed cell foam with a rubber adhesive that provides high initial adhesion to a variety of surfaces in.. |
|||
Tensile Strength at Break | 0.415 MPa | 60.2 psi | Dynamic, 1 in.<sup>2</sup> (6.45 cm<sup>2</sup>) overlap Jaw Speed 0.5 in./min (12.7 mm/min.); ASTM D-897 |
3M 4492B Double Coated Polyethylene Foam Tape 3M™ Double Coated Polyethylene Foam Tapes 4462W, 4462B, 4466W and 4466B combine a conformable closed cell foam with a rubber adhesive that provides high initial adhesion to a variety of surfaces in.. |
|||
Tensile Strength at Break | 0.415 MPa | 60.2 psi | Dynamic, 1 in.<sup>2</sup> (6.45 cm<sup>2</sup>) overlap Jaw Speed 0.5 in./min (12.7 mm/min.); ASTM D-897 |
3M 4462W Double Coated Polyethylene Foam Tape 3M™ Double Coated Polyethylene Foam Tapes 4462W, 4462B, 4466W and 4466B combine a conformable closed cell foam with a rubber adhesive that provides high initial adhesion to a variety of surfaces in.. |
|||
Tensile Strength at Break | 0.415 MPa | 60.2 psi | Dynamic, 1 in.<sup>2</sup> (6.45 cm<sup>2</sup>) overlap Jaw Speed 0.5 in./min (12.7 mm/min.); ASTM D-897 |
3M 4492G Double Coated Polyethylene Foam Tape 3M™ Double Coated Polyethylene Foam Tapes 4462W, 4462B, 4466W and 4466B combine a conformable closed cell foam with a rubber adhesive that provides high initial adhesion to a variety of surfaces in.. |
|||
Tensile Strength at Break | 0.415 MPa | 60.2 psi | Dynamic, 1 in.<sup>2</sup> (6.45 cm<sup>2</sup>) overlap Jaw Speed 0.5 in./min (12.7 mm/min.); ASTM D-897 |
3M 4492W Double Coated Polyethylene Foam Tape 3M™ Double Coated Polyethylene Foam Tapes 4462W, 4462B, 4466W and 4466B combine a conformable closed cell foam with a rubber adhesive that provides high initial adhesion to a variety of surfaces in.. |