Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 758 MPa @Temperature 232 °C |
110000 psi @Temperature 450 °F |
Phase II (Prepreg stored in freezer 4 months at -9°C and exposed to 60 days at RT) |
Hexcel® HexPly® F650 Bismaleimide Resin with Graphite F3T584 fabric reinforcement Aging Data, (T300-3K, 8 H.S.); Laminate Physicals: 59.6% Fiber volume, 34.0% Resin content, 1.0% VoidsInformation provided by HexCel |
|||
Flexural Yield Strength | 758 MPa @Temperature 232 °C |
110000 psi @Temperature 450 °F |
T300; Fill Flexure; AMB |
Hexcel® HexPly® M65 Bismaleimide Resin, Carbon Fabric Form Fibers: T300-3K, AS4C-3KInformation provided by HexCel |
|||
Flexural Yield Strength | 758 MPa @Temperature 177 °C |
110000 psi @Temperature 351 °F |
IM7 (12K); [0°, 90°]5s; Wet condition |
Hexcel® HexPly® M65 Bismaleimide Resin, Carbon Tape Form Fiber: IM7-12KInformation provided by HexCel |