Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Bend Radius, Minimum | >= 0.00 t | >= 0.00 t | thickness between 0.5 and 3.0 mm |
SSAB Tunnplat Docol® 220 RP High-strength Steel High-strength SteelComments: Docol RP - Cold Rolled Steel - rephosphorized steel. Property values are for cold-rolled steel; thicknesses 0.40 - 3.0 mm. Iron content is approximate - exact compositi.. |
|||
Bend Radius, Minimum | >= 0.00 t | >= 0.00 t | thickness between 0.5 and 3.0 mm |
SSAB Tunnplat Docol® 260 RP High-strength Steel High-strength SteelComments: Docol RP - Cold Rolled Steel - rephosphorized steel. Property values are for cold-rolled steel; thicknesses 0.40 - 3.0 mm. Iron content is approximate - exact compositi.. |
|||
Bend Radius, Minimum | >= 0.00 t @Thickness 0.500 - 3.00 mm |
>= 0.00 t @Thickness 0.0197 - 0.118 in |
|
SSAB Tunnplat Docol® 280YP High-strength Steel High-strength SteelComments: Docol YP - Cold Rolled Steel - HSLA. Property values are for cold-rolled steel; thicknesses 0.5 - 3.00 mm. Iron content is approximate - exact composition is not report.. |
|||
Bend Radius, Minimum | >= 0.00 t | >= 0.00 t | thickness between 0.5 and 3.0 mm |
SSAB Tunnplat Docol® 300 RP High-strength Steel High-strength SteelComments: Docol RP - Cold Rolled Steel - rephosphorized steel. Property values are for cold-rolled steel; thicknesses 0.40 - 3.0 mm. Iron content is approximate - exact compositi.. |
|||
Bend Radius, Minimum | >= 0.00 t @Thickness 0.500 - 3.00 mm |
>= 0.00 t @Thickness 0.0197 - 0.118 in |
|
SSAB Tunnplat Docol® 350YP High-strength Steel High-strength SteelComments: Docol YP - Cold Rolled Steel - HSLA. Property values are for cold-rolled steel; thicknesses 0.5 - 3.00 mm. Iron content is approximate - exact composition is not report.. |
|||
Bend Radius, Minimum | >= 0.00 t | >= 0.00 t | thickness between 1.0 and 1.5 mm |
SSAB Tunnplat Docol® 400DP High-strength Steel High-strength SteelComments: Docol DP - Cold Rolled Steel - dual-phase steel. Property values are for cold-rolled steel; thicknesses 0.5 - 1.6 mm. Iron content is approximate - exact composition is.. |
|||
Bend Radius, Minimum | >= 0.00 t | >= 0.00 t | thickness between 0.5 and 2.5 mm |
SSAB Tunnplat Docol® 420YP High-strength Steel High-strength SteelComments: Docol YP - Cold Rolled Steel - HSLA. Property values are for cold-rolled steel; thicknesses 0.5 - 3.00 mm. Iron content is approximate - exact composition is not report.. |
|||
Bend Radius, Minimum | >= 0.00 t | >= 0.00 t | thickness between 1.0 and 1.5 mm |
SSAB Tunnplat Docol® 500DP High-strength Steel High-strength SteelComments: Docol DP - Cold Rolled Steel - dual-phase steel. Property values are for cold-rolled steel; thicknesses 0.5 - 1.6 mm. Iron content is approximate - exact composition is.. |
|||
Bend Radius, Minimum | >= 0.00 t | >= 0.00 t | t = 1.0 mm |
SSAB Tunnplat Docol® 500YP High-strength Steel High-strength SteelComments: Docol YP - Cold Rolled Steel - HSLA. Property values are for cold-rolled steel; thicknesses 0.5 - 3.00 mm. Iron content is approximate - exact composition is not report.. |
|||
Bend Radius, Minimum | >= 0.00 t | >= 0.00 t | t = 1.0 mm |
SSAB Tunnplat Docol® 600DL High-strength Steel High-strength SteelComments: Docol DP - Cold Rolled Steel - Extra high-strength steel (EHS). Property values are for cold-rolled steel; thicknesses 0.5 - 1.6 mm. Iron content is approximate - exact.. |
|||
Bend Radius, Minimum | >= 0.00 t @Thickness 3.20 mm |
>= 0.00 t @Thickness 0.126 in |
|
SSAB Tunnplat Docol® 600DP High-strength Steel High-strength SteelComments: Docol DP - Cold Rolled Steel - Extra high-strength steel (EHS). Property values are for cold-rolled steel; thicknesses 0.5 - 1.6 mm. Iron content is approximate - exact.. |
|||
Bend Radius, Minimum | >= 0.00 t @Thickness 0.500 - 3.00 mm |
>= 0.00 t @Thickness 0.0197 - 0.118 in |
|
SSAB Tunnplat Docol® 220 YP High-strength Steel High-strength SteelComments: Docol YP - Cold Rolled Steel - HSLA. Property values are for cold-rolled steel; thicknesses 0.5 - 3.00 mm. Iron content is approximate - exact composition is not report.. |
|||
Bend Radius, Minimum | 0.00 t | 0.00 t | ISO 7438 |
ThyssenKrupp PAS 315 Structural Steel for Cold Forming This Material Specification applies to plates made of low carbon high strength steels with minimum yield strength values between 315 and 700 MPa1) in the thermo mechanically rolled delivery conditio.. |