Polymer Property : Film Tensile Strength at Break, TD = 7540 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, TD	52.0 MPa @Thickness 0.0200 mm	7540 psi @Thickness 0.000787 in	ISO 527-3
Total MDPE HF 513 Medium Density Polyethylene, Blown Film MDPE HF 513 is a medium density polyethylene produced by slurry loop low pressure process with hexene as co-monomer.MDPE HF 513 is a semi-high molecular weight polyethylene giving excellent mechanic..
Film Tensile Strength at Break, TD	52.0 MPa @Thickness 0.0400 mm	7540 psi @Thickness 0.00157 in	ISO 527-3
Total MDPE HF 513 Medium Density Polyethylene, Blown Film MDPE HF 513 is a medium density polyethylene produced by slurry loop low pressure process with hexene as co-monomer.MDPE HF 513 is a semi-high molecular weight polyethylene giving excellent mechanic..
Film Tensile Strength at Break, TD	52.0 MPa @Thickness 0.0400 mm	7540 psi @Thickness 0.00157 in	ISO 527-3
Total MDPE HT 514 Medium Density Polyethylene, Blown Film MDPE HT 514 is a medium density polyethylene produced by slurry loop low pressure process with hexene as co-monomer.MDPE HT 514 is a semi-high molecular weight polyethylene giving excellent mechanic..