Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Compressive Modulus | 2.00 GPa | 290 ksi | Sample Type A, 1 mm/min; ISO 604:2002 |
Global EPP PA 612 Copolymer Cast Polyamide 612 Cast nylons are generally accepted as the primary engineering polymer, suitable for virtually any plain bearing application. By varying the conditions of polymerisation the mechanical properties of .. |
|||
Compressive Modulus | 2.00 GPa | 290 ksi | ASTM D695 |
Saint-Gobain Meldin® 7022 DF Direct Formed Graphite Filled Polyimide Melidin® 7022 DF is a direct formed polyimide that contains 40% graphite filler. This grade offers additional dimensional stability at elevated temperatures and the lowest CTE of any Meldin® .. |
|||
Compressive Modulus | 2.00 GPa | 290 ksi | ASTM D695 |
Saint-Gobain Meldin® 7001 Direct Formed Polyimide Finished parts and basic shapes made from unfilled polyimide material for structural applications requiring requiring high electrical insulative properties, high purity and low outgassing, and high .. |
|||
Compressive Modulus | 2.00 GPa | 290 ksi | ASTM D695 |
Saint-Gobain Meldin® 7001 Isostatically Molded Polyimide Finished parts and basic shapes made from unfilled polyimide material for structural applications requiring requiring high electrical insulative properties, high purity and low outgassing, and high .. |
|||
Compressive Modulus | 2.00 GPa | 290 ksi | |
CMT Materials CTB 44 Composite Toolboard High Temperature CTB-44 is manufactured by CMT Materials for a wide variety of vacuum forming applications. It is suitable for use up to 2500F (1210C). CTB-44 utilizes a copolymer base material and smaller cell st.. |