Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Compressive Modulus | 16.5 GPa @Temperature 23.9 °C |
2400 ksi @Temperature 75.0 °F |
Dry; 325°F, 1000psi Cured; ASTM D695 |
Park Electrochemical Nelcote® F-502 Phenolic Prepreg, Silica Reinforced Nelcote® F-502 is a MIL-R-9299 phenolic resin system suitable for impregnation on any MIL-C-9084 fabric with a compatible finish. F-502 is used in the manufacture of ablative reinforcements in rock.. |
|||
Compressive Modulus | 16.5 GPa @Temperature 23.9 °C |
2400 ksi @Temperature 75.0 °F |
Dry; 325°F Autoclave; ASTM D695 |
Park Electrochemical Nelcote® F-554 Phenolic Prepreg, Aerospace Silica Fabric Reinforced Nelcote® F-554 is a high purity silica filled phenolic resin coated on Commercial or Aerospace grade silica fabric. F-554 is used in the manufacture of intermediate temperature ablative rocket nozz.. |
|||
Compressive Modulus | 16.5 GPa @Temperature 23.9 °C |
2400 ksi @Temperature 75.0 °F |
Dry; 325°F Autoclave; ASTM D695 |
Park Electrochemical Nelcote® F-557 Phenolic Prepreg, Commercial Silica Fabric Reinforced Nelcote® F-557 is a high purity silica filler phonic resin coated on Commercial or Aerospace grade silica fabric. F-557 is used in the manufacture of intermediate temperature ablative rocket nozzle.. |
|||
Compressive Modulus | 16.5 GPa | 2390 ksi | 90º, RT, Dry; DIN65380 |
Hexcel® HexPly® M12 135°C Curing Epoxy Matrix, TVR380/26% Fiber Information provided by HexCel |