Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Compressive Yield Strength | 70.0 - 300 MPa | 10200 - 43500 psi | Average value: 180 MPa Grade Count:25 |
Overview of materials for Phenolic, Novolac, Cellulose Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Cellulose Filled". Each property range of values reported is minimum and maximum valu.. |
|||
Compressive Yield Strength | >= 70.0 MPa | >= 10200 psi | 1st Grade, 2nd Grade |
Kazanorgsintez PC-005 Polycarbonate Production Method: Obtained by means of polycondensation method. Application: Intended for product manufacture by method of extrusion and die-casting.Information Provided by Kazanorgsintez |
|||
Compressive Yield Strength | >= 70.0 MPa | >= 10200 psi | |
Kazanorgsintez PC-007 Polycarbonate Production Method: Obtained by means of polycondensation method. Application: Intended for product manufacture by method of extrusion and die-casting.Information Provided by Kazanorgsintez |
|||
Compressive Yield Strength | >= 70.0 MPa | >= 10200 psi | 1st Grade, 2nd Grade |
Kazanorgsintez PC-010 Polycarbonate Production Method: Obtained by means of polycondensation method. Application: Intended for product manufacture by method of die-casting.Information Provided by Kazanorgsintez |
|||
Compressive Yield Strength | 70.0 MPa | 10200 psi | at 5% deformation, parallel to thickness |
Zircar Refractory Composites ZIRCAL-45 Refractory Board Type ZIRCAL-45 Refractory Board is a self supporting, high strength, rigid refractory product fabricated from calcium silicate, inert fillers and reinforcing agents. Its high structural strength com.. |
|||
Compressive Yield Strength | 70.0 MPa @Strain 10.0 %, Temperature 23.0 °C |
10200 psi @Strain 10.0 %, Temperature 73.4 °F |
EN ISO 604 |
Ensinger TECASINT 3062 Polyimide, Shiny Black, 15% Graphite, 10% PTFE (PI) TECASINT is a range of non-melting high temperature polyimides characterized by high strength over a wide range of temperatures, good long term thermal stability, minimal thermal expansion and excel.. |
|||
Compressive Yield Strength | 70.0 - 268 MPa | 10200 - 38900 psi | Average value: 160 MPa Grade Count:15 |
Overview of materials for Polyimide, Graphite Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyimide, Graphite Filled". Each property range of values reported is minimum and maximum values of app.. |