Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Compressive Yield Strength | 27.6 MPa | 4000 psi | TM R050-38 |
Resinlab® EP965LVLX Black Unfilled Electronic Grade Epoxy Encapsulant Resinlab™ EP965LVLX Black is a two part unfilled electronic grade epoxy encapsulant designed for small to medium sized castings. It cures at room temperature to a tough, semi-rigid polymer. It has .. |
|||
Compressive Yield Strength | 27.6 - 47.6 MPa | 4000 - 6900 psi | Average value: 40.9 MPa Grade Count:3 |
Overview of materials for Polypropylene with 20% Calcium Carbonate (CaCO3) Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 20% Calcium Carbonate (CaCO3) Filler". Each property range of values reported is mini.. |
|||
Compressive Yield Strength | 27.6 MPa | 4000 psi | TM R050-38 |
Resinlab® EP1026 Clear Epoxy Adhesive Resinlab™ EP1026 Clear is a two part unfilled epoxy adhesive designed for high speed bonding of metals, ceramics, and most plastics. It cures to a tough semi-rigid material, and is free flowing in .. |
|||
Compressive Yield Strength | 27.6 MPa | 4000 psi | TM R050-38 |
Resinlab® EP1200 Black Casting Resin Resinlab™ EP1200 Black is a highly filled, medium viscosity black casting resin designed for applications requiring a high degree of thermal conductivity, flexibility and a low CTE. It meets the re.. |
|||
Compressive Yield Strength | 27.6 MPa | 4000 psi | TM R050-38 |
Resinlab® EP965LVLX Clear Unfilled Electronic Grade Epoxy Encapsulant Resinlab™ EP965LVLX Clear is a two part unfilled electronic grade epoxy encapsulant designed for small to medium sized castings. It cures at room temperature to a tough, semi-rigid polymer. It has .. |
|||
Compressive Yield Strength | 27.6 MPa | 4000 psi | TM R050-38 |
Resinlab® EP1026 Black Epoxy Adhesive Resinlab™ EP1026 Black is a two part unfilled epoxy adhesive designed for high speed bonding of metals, ceramics, and most plastics. It cures to a tough semi-rigid material, and is free flowing in .. |