Polymer Property : Compressive Yield Strength = 240 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Compressive Yield Strength	240 MPa	34800 psi	ASTM D695
Solvay Specialty Polymers Ryton® R-4-230NA Polyphenylene Sulfide Compound (Unverified Data**) Natural Color Polyphenylene Sulfide CompoundRyton® R-4-230NA is an advanced 40% fiberglass reinforced polyphenylene sulfide compound which provides reduced flash and improved processability compare..
Compressive Yield Strength	240 MPa	34800 psi	ASTM D695
Solvay Specialty Polymers Ryton® R-4-230BL Polyphenylene Sulfide Compound (Unverified Data**) Black Polyphenylene Sulfide CompoundRyton® R-4-230BL is an advanced 40% fiberglass reinforced polyphenylene sulfide compound which provides reduced flash and improved processability compared to oth..
Compressive Yield Strength	240 MPa	34800 psi	ASTM D695
Solvay Specialty Polymers Ryton® R-4 Polyphenylene Sulfide Compound (Unverified Data**) Natural Color Polyphenylene Sulfide CompoundRyton® R-4 is a 40% fiberglass reinforced polyphenylene sulfide compound which provides outstanding chemical resistance and mechanical properties even at..
Compressive Yield Strength	240 MPa	34800 psi	ASTM D695
Solvay Specialty Polymers Ryton® R-4 02 Polyphenylene Sulfide Compound (Unverified Data**) Black Polyphenylene Sulfide CompoundRyton® R-4 02 is a 40% fiberglass reinforced polyphenylene sulfide compound which provides outstanding chemical resistance and mechanical properties even at elev..
Compressive Yield Strength	240 MPa	34800 psi	ASTM D695
Solvay Specialty Polymers Ryton® R-7-120NA Polyphenylene Sulfide Compound (Unverified Data**) Natural Color Polyphenylene Sulfide CompoundRyton® R-7-120NA is an advanced glass/mineral filled polyphenylene sulfide compound developed to provide good weldline strength and low maintenance moldi..
Compressive Yield Strength	240 MPa	34800 psi	ASTM D695
Solvay Specialty Polymers Ryton® R-7-120BL Polyphenylene Sulfide Compound (Unverified Data**) Black Polyphenylene Sulfide CompoundRyton® R-7-120BL is an advanced glass/mineral filled polyphenylene sulfide compound developed to provide good weldline strength and low maintenance molding using..
Compressive Yield Strength	240 MPa	34800 psi	ASTM D695
Chevron Phillips Ryton® R10-110BL Polyphenylene Sulfide Compound (discontinued **) Black Polyphenylene Sulfide CompoundRyton® R10-110BL is a glass and mineral filled polyphenylene sulfide compound which provides a good combination of mechanical and electrical properties.Applicati..
Compressive Yield Strength	240 MPa	34800 psi	ASTM D695
Chevron Phillips Ryton® R-7 Polyphenylene Sulfide Compound (discontinued **) Natural Color Polyphenylene Sulfide CompoundRyton® R-7 is polyphenylene sulfide compounded with glass fibers and mineral fibers to produce an injection moldable high temperature engineering compoun..
Compressive Yield Strength	240 MPa	34800 psi	0°
Hexcel® HexPly® ES 84 120°C Curing Epoxy Matrix, Aramid Balanced fabric 175 g/m2 Information provided by HexCel
Compressive Yield Strength	240 MPa	34800 psi	Compression After Impact @ 6.6 J/mm, Results normalized to 60% fibre volume for Carbon, 50% fibre volume for Kevlar; pr EN 6038
Hexcel® HexPly® 920CX-FM40J-6-42% 125°C Curing Epoxy Matrix High modulus carbon, Unidirectional, 165 g/m2Information provided by HexCel
Compressive Yield Strength	240 MPa	34800 psi	10% Strain; EN ISO 604
Ensinger TECASINT 1011 Polyimide (PI) TECASINT is a range of non-melting high temperature polyimides characterized by high strength over a wide range of temperatures, good long term thermal stability, minimal thermal expansion and excel..
Compressive Yield Strength	240 MPa	34800 psi	ASTM D695
Chevron Phillips Ryton® R-7 02 Polyphenylene Sulfide Compound (discontinued **) Black Polyphenylene Sulfide CompoundRyton® R-7 02 is polyphenylene sulfide compounded with glass fibers and mineral fibers to produce an injection moldable high temperature engineering compound wit..