Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 5000 MPa | 725000 psi | (Fracture) @58HRC, Tempering: 3 x 1 h at 1040°F; Four-point bend |
Bohler-Uddeholm UDDEHOLM VANADIS 23 (AISI M3:2) Hot Work Tool Steel Chromium-molybdenum-tungsten-vanadium alloyed PM steelVanadis 23 is a high speed powder metallurgical steel, recommended for low temperature die casting applications and warm forging applications wh.. |
|||
Flexural Strength | 5000 MPa | 725000 psi | 58 HRC. Four point bend testing. 5 mm ø. 5mm/min. Austenitizing temperature: 990-1180°C, Tempering: 3X1 h at 560°C |
Assab Steels ASP 23 Cold Work Steel ASP 23 is a chromium-molybdenum-tungsten-vanadium alloyed high speed steel which is characterized by:High wear resistance (abrasive profile)High compressive strengthVery good through-hardening prope.. |
|||
Flexural Strength | 5000 MPa @Diameter 5.00 mm |
725000 psi @Diameter 0.197 in |
66 HRC. Four point bend testing. 5mm/min. Austenitizing temperature: 990-1180°C, Tempering: 3X1 h at 560°C |
Assab Steels ASP 23 Cold Work Steel ASP 23 is a chromium-molybdenum-tungsten-vanadium alloyed high speed steel which is characterized by:High wear resistance (abrasive profile)High compressive strengthVery good through-hardening prope.. |