Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 301 MPa | 43700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP EX03647H PEI LNP LUBRICOMP* EX03647H is a compound based on Polyetherimide resin containing Proprietary Fillers. Added features of this material include: Healthcare, Wear Resistant. |
|||
Flexural Strength | 301 MPa | 43600 psi | ASTM D790 |
Techmer ES HiFill® PA6 GF HS UV 33% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcements, 33% Filler by WeightAdditive: Lubricant, Heat Stabilizer and UV Stabilizer Features: Lubricated, Good UV Re.. |
|||
Flexural Strength | 301 MPa | 43600 psi | ASTM D790 |
Techmer ES HiFill® PA6 GF33 HS L 33% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 33% Filler by WeightAdditive: Lubricant and Heat StabilizerFeatures: Heat Stabilized and LubricatedInformati.. |
|||
Flexural Strength | 301 MPa | 43700 psi | ISO 178 |
SABIC Innovative Plastics LNP VERTON RV008ES PA 66 LNP* VERTON* RV008ES is a compound based on Nylon 66 resin containing 40% Long Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized, Structural. |
|||
Flexural Strength | 301 MPa | 43700 psi | ISO 178 |
SABIC Innovative Plastics LNP VERTON RV008ES PA 66 (Asia Pacific) LNP* Verton* RV008ES is a compound based on Nylon 66 resin containing Long Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized. |