Polymer Property : Modulus of Elasticity = 31600 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Modulus of Elasticity	218 GPa @Temperature 27.0 Â°C	31600 ksi @Temperature 80.6 Â°F
Haynes R-41 alloy, Vacuum melted, exceptionally high strength at temperature between 649-982Â°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Modulus of Elasticity	218 GPa @Temperature 25.0 Â°C	31600 ksi @Temperature 77.0 Â°F
Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079Â°C, water quenched, 30 minutes at 1066Â°C, air cooled, aged 16 hours at 760Â°C (1400Â°F) Vacuum melted, exceptionally high strength at temperature between 649-982Â°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Modulus of Elasticity	218 GPa @Temperature 21.0 Â°C	31600 ksi @Temperature 69.8 Â°F
Haynes R-41 alloy, sheet 0.762-2.54 mm exclusive, 30 minutes at 1066Â°C, air cooled, aged 16 hours at 760Â°C (1400Â°F) Vacuum melted, exceptionally high strength at temperature between 649-982Â°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Modulus of Elasticity	218 GPa @Temperature 21.0 Â°C	31600 ksi @Temperature 69.8 Â°F
Haynes R-41 alloy, sheet 0.762-2.54 mm exclusive, 30 minutes at 1121Â°C, air cooled, aged 16 hours at 899Â°C Vacuum melted, exceptionally high strength at temperature between 649-982Â°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Modulus of Elasticity	218 GPa @Temperature 100 Â°C	31600 ksi @Temperature 212 Â°F	Dynamic
Haynes HastelloyÂ® C-22HSâ„¢ Nickel Alloy Gas Tungsten Arc Welded (GTAW) All Weld Cruciform Outstanding Corrosion Resistance, High Strength HASTELLOYÂ® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou..
Modulus of Elasticity	218 GPa @Temperature 100 Â°C	31600 ksi @Temperature 212 Â°F	Dynamic
Haynes HastelloyÂ® C-22HSâ„¢ Nickel Alloy Gas Tungsten Arc Welded (GTAW) Plate Outstanding Corrosion Resistance, High Strength HASTELLOYÂ® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou..
Modulus of Elasticity	218 GPa @Temperature 100 Â°C	31600 ksi @Temperature 212 Â°F	Dynamic
Haynes HastelloyÂ® C-22HSâ„¢ Nickel Alloy Gas Tungsten Arc Welded (GTAW) Sheet Outstanding Corrosion Resistance, High Strength HASTELLOYÂ® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou..
Modulus of Elasticity	218 GPa @Temperature 100 Â°C	31600 ksi @Temperature 212 Â°F	Dynamic
Haynes HastelloyÂ® C-22HSâ„¢ Nickel Alloy Plate and Bar, Hot-rolled, Solution Annealed Outstanding Corrosion Resistance, High Strength HASTELLOYÂ® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou..
Modulus of Elasticity	218 GPa @Temperature 100 Â°C	31600 ksi @Temperature 212 Â°F	Dynamic
Haynes HastelloyÂ® C-22HSâ„¢ Nickel Alloy Plate, Age-hardened Outstanding Corrosion Resistance, High Strength HASTELLOYÂ® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou..
Modulus of Elasticity	218 GPa @Temperature 100 Â°C	31600 ksi @Temperature 212 Â°F	Dynamic
Haynes HastelloyÂ® C-22HSâ„¢ Nickel Alloy Plate, Annealed Outstanding Corrosion Resistance, High Strength HASTELLOYÂ® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou..
Modulus of Elasticity	218 GPa @Temperature 100 Â°C	31600 ksi @Temperature 212 Â°F	Dynamic
Haynes HastelloyÂ® C-22HSâ„¢ Nickel Alloy Sheet, Cold-rolled, Solution Annealed Outstanding Corrosion Resistance, High Strength HASTELLOYÂ® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou..
Modulus of Elasticity	218 GPa @Temperature 100 Â°C	31600 ksi @Temperature 212 Â°F	Dynamic
Haynes HastelloyÂ® C-22HSâ„¢ Nickel Alloy Sheet, Cold-rolled, Solution Annealed, Age-hardened Outstanding Corrosion Resistance, High Strength HASTELLOYÂ® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou..
Modulus of Elasticity	218 GPa @Temperature 100 Â°C	31600 ksi @Temperature 212 Â°F	Dynamic
Haynes HastelloyÂ® C-22HSâ„¢ Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform Outstanding Corrosion Resistance, High Strength HASTELLOYÂ® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou..
Modulus of Elasticity	218 GPa @Temperature 100 Â°C	31600 ksi @Temperature 212 Â°F
Special Metals INCONELÂ® alloy 740 Precipitation-Hardenable Ni-Cr-Co Superalloy INCONELÂ® alloy 740 is a nickel-chromium-cobalt alloy developed by Special Metals Corporation. The alloy is age hardenable by the precipitation of a gamma prime second phase. Potential applicati..
Modulus of Elasticity	218 GPa @Temperature 20.0 °C	31600 ksi @Temperature 68.0 °F
Bohler-Uddeholm BÖHLER M303 EXTRA Plastic Mold Steel BOHLER M303 EXTRA is a stainless martensitic chromium steel, offering excellent toughness, corrosion and wear resistance. It is characterized by improved machinability and polishability. BOHLER M303..
Modulus of Elasticity	218 GPa @Temperature 100 °C	31600 ksi @Temperature 212 °F	Dynamic
Haynes Hastelloy® C-22HS™ Nickel Alloy Plate and Bar, Hot-rolled, Solution Annealed, Age-hardened Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately doubl..
Modulus of Elasticity	218 GPa @Temperature 100 °C	31600 ksi @Temperature 212 °F	Dynamic
Haynes Hastelloy® C-22HS™ Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately doubl..
Modulus of Elasticity	218 GPa @Temperature 27.0 °C	31600 ksi @Temperature 80.6 °F
Haynes R-41 alloy, Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications include ..