Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Modulus of Elasticity	150 GPa @Temperature 927 Â°C	21800 ksi @Temperature 1700 Â°F
Haynes R-41 alloy, Vacuum melted, exceptionally high strength at temperature between 649-982Â°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Modulus of Elasticity	150 GPa @Temperature 927 Â°C	21800 ksi @Temperature 1700 Â°F
Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079Â°C, water quenched, 30 minutes at 1066Â°C, air cooled, aged 16 hours at 760Â°C (1400Â°F) Vacuum melted, exceptionally high strength at temperature between 649-982Â°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Modulus of Elasticity	150 GPa @Temperature 927 Â°C	21800 ksi @Temperature 1700 Â°F
Haynes R-41 alloy, sheet 0.762-2.54 mm exclusive, 30 minutes at 1066Â°C, air cooled, aged 16 hours at 760Â°C (1400Â°F) Vacuum melted, exceptionally high strength at temperature between 649-982Â°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Modulus of Elasticity	150 GPa @Temperature 927 Â°C	21800 ksi @Temperature 1700 Â°F
Haynes R-41 alloy, sheet 0.762-2.54 mm exclusive, 30 minutes at 1121Â°C, air cooled, aged 16 hours at 899Â°C Vacuum melted, exceptionally high strength at temperature between 649-982Â°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Modulus of Elasticity	150 GPa @Temperature 500 °C	21800 ksi @Temperature 932 °F	Typical annealed sample; short time elevated temp.
American Utility Metals Cromgard® Stainless Steel Cromgard is a low cost stainless steel, which is able to provide benefits of good weldability and formability, making it capable of fabrication by conventional techniques. It provides the benefits o..
Modulus of Elasticity	150 GPa @Temperature 927 °C	21800 ksi @Temperature 1700 °F
Haynes R-41 alloy, Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications include ..