Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Modulus of Elasticity | 194 GPa @Temperature 357 °C |
28100 ksi @Temperature 675 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, flat products Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 194 GPa @Temperature 357 °C |
28100 ksi @Temperature 675 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 194 GPa @Temperature 357 °C |
28100 ksi @Temperature 675 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 194 GPa @Temperature 357 °C |
28100 ksi @Temperature 675 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 194 GPa @Temperature 357 °C |
28100 ksi @Temperature 675 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 194 GPa @Temperature 357 °C |
28100 ksi @Temperature 675 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 194 GPa @Temperature 357 °C |
28100 ksi @Temperature 675 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 194 GPa @Temperature 357 °C |
28100 ksi @Temperature 675 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 194 GPa @Temperature 357 °C |
28100 ksi @Temperature 675 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 194 GPa @Temperature 357 °C |
28100 ksi @Temperature 675 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 194 GPa @Temperature 357 °C |
28100 ksi @Temperature 675 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 194 GPa @Temperature 357 °C |
28100 ksi @Temperature 675 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 194 GPa @Temperature 357 °C |
28100 ksi @Temperature 675 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged at 649°C (1200°F) for 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 194 GPa @Temperature 357 °C |
28100 ksi @Temperature 675 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, gas tungsten arc welded, aged at 538°C (1000°F) for 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 194 GPa @Temperature 357 °C |
28100 ksi @Temperature 675 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 194 GPa @Temperature 357 °C |
28100 ksi @Temperature 675 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 194 GPa @Temperature 357 °C |
28100 ksi @Temperature 675 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 194 GPa @Temperature 357 °C |
28100 ksi @Temperature 675 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 194 GPa @Temperature 357 °C |
28100 ksi @Temperature 675 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 194 GPa @Temperature 357 °C |
28100 ksi @Temperature 675 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 194 GPa @Temperature 357 °C |
28100 ksi @Temperature 675 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, weld metal, aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 194 GPa @Temperature 357 °C |
28100 ksi @Temperature 675 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, weld metal, aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 194 GPa @Temperature 357 °C |
28100 ksi @Temperature 675 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, weld metal, aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 194 GPa @Temperature 357 °C |
28100 ksi @Temperature 675 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, weld metal, aged at 649°C (1200°F) for 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 194 GPa @Temperature 100 °C |
28100 ksi @Temperature 212 °F |
|
Special Metals INCONEL® alloy 693 INCONEL alloy 693 is a new alloy from Special Metals which offers resistance to high temperature corrosion mechanisms not previously available from a nickel-based alloy. Of particular interest to t.. |
|||
Modulus of Elasticity | 194 GPa @Temperature 400 °C |
28100 ksi @Temperature 752 °F |
|
Special Metals INCONEL® alloy N06230 Ni-Cr-W-Mo Alloy INCONEL® alloy N06230 (UNS N06230 / W.Nr. 2.4733) is a carbide strengthened nickel-chromium-tungsten-molybdenum alloy with an exceptional combination of strength, stability, and resistance to cor.. |
|||
Modulus of Elasticity | 194 GPa @Temperature 357 °C |
28100 ksi @Temperature 675 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
Modulus of Elasticity | 194 GPa @Temperature 357 °C |
28100 ksi @Temperature 675 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
Modulus of Elasticity | 194 GPa @Temperature 357 °C |
28100 ksi @Temperature 675 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
Modulus of Elasticity | 194 GPa @Temperature 357 °C |
28100 ksi @Temperature 675 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |