Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Impact Test | 54.2 J @Temperature 22.8 °C |
40.0 ft-lb @Temperature 73.0 °F |
Dynatup Instrumented Impact; ASTM D3763 |
Spartech Royalite R6000 FR-PC Aircraft Grade Sheet Description: Aircraft Grade SheetInformation provided by Spartech. |
|||
Impact Test | 54.2 J | 40.0 ft-lb | |
Schmolz + Bickenbach MoldMAX® SC Copper Alloy Description: Brush Wellman’s MoldMAX® SC is a high conductivity copper mold alloy with good strength. MoldMAX® SC is used as blow mold cavities, injection mold cores and cavities and hot .. |
|||
Impact Test | 54.2 J @Thickness 3.17 mm, Temperature -40.0 °C |
40.0 ft-lb @Thickness 0.125 in, Temperature -40.0 °F |
ARM impact |
A. Schulman POLYAXIS® CP813-31 General-Purpose Polyethylene DescriptionPolyaxis CP 813-31 is a general-purpose black linear low density polyethylene compound offering quick cycles and part to part consistency. NOTE: Physical properties are based on rotationa.. |
|||
Impact Test | 54.2 J @Thickness 3.17 mm, Temperature -40.0 °C |
40.0 ft-lb @Thickness 0.125 in, Temperature -40.0 °F |
ARM impact |
A. Schulman POLYAXIS® CP813-31 General-Purpose Polyethylene DescriptionPolyaxis CP 813-31 is a general-purpose black linear low density polyethylene compound offering quick cycles and part to part consistency. NOTE: Physical properties are based on rotationa.. |
|||
Impact Test | 54.2 J @Thickness 3.17 mm, Temperature -40.0 °C |
40.0 ft-lb @Thickness 0.125 in, Temperature -40.0 °F |
ARM impact |
A. Schulman POLYAXIS® CP813-31 General-Purpose Polyethylene DescriptionPolyaxis CP 813-31 is a general-purpose black linear low density polyethylene compound offering quick cycles and part to part consistency. NOTE: Physical properties are based on rotationa.. |
|||
Impact Test | 54.2 J @Thickness 3.17 mm, Temperature -40.0 °C |
40.0 ft-lb @Thickness 0.125 in, Temperature -40.0 °F |
ARM impact |
A. Schulman POLYAXIS® CP813-31 General-Purpose Polyethylene DescriptionPolyaxis CP 813-31 is a general-purpose black linear low density polyethylene compound offering quick cycles and part to part consistency. NOTE: Physical properties are based on rotationa.. |
|||
Impact Test | 54.2 J @Thickness 3.17 mm, Temperature -40.0 °C |
40.0 ft-lb @Thickness 0.125 in, Temperature -40.0 °F |
ARM impact |
A. Schulman POLYAXIS® CP813-31 General-Purpose Polyethylene DescriptionPolyaxis CP 813-31 is a general-purpose black linear low density polyethylene compound offering quick cycles and part to part consistency. NOTE: Physical properties are based on rotationa.. |
|||
Impact Test | 54.2 J | 40.0 ft-lb | Torque Strength; curing at 1000°F |
Aremco Ceramabond™ 885 High Temperature Ceramic Adhesive/Paste, Zirconia Filled Aremco's ceramic adhesives are easy to use, one- and two-component systems which air dry in 1-2 hrs and are ready for use following a 200 to 700 °F cure. These materials are mostly water-based and.. |
|||
Impact Test | 54.2 J | 40.0 ft-lb | Torque Strength; curing at 1000°F |
Aremco Ceramabond™ 890 High Temperature Ceramic Adhesive/Paste, Silicon Carbide Filled Aremco's ceramic adhesives are easy to use, one- and two-component systems which air dry in 1-2 hrs and are ready for use following a 200 to 700 °F cure. These materials are mostly water-based and.. |
|||
Impact Test | 54.2 J @Thickness 3.17 mm, Temperature -40.0 °C |
40.0 ft-lb @Thickness 0.125 in, Temperature -40.0 °F |
ARM impact |
A. Schulman POLYAXIS® CP813-31 General-Purpose Polyethylene DescriptionPolyaxis CP 813-31 is a general-purpose black linear low density polyethylene compound offering quick cycles and part to part consistency. NOTE: Physical properties are based on rotationa.. |